High temperature deformation behavior of Al 2124-SiCp composite

被引:22
作者
Han, BQ
Chan, KC
Yue, TM
Lau, WS
机构
[1] Dept. of Manufacturing Engineering, Hong Kong Polytechnic University, Hung Horn, Kowloon
关键词
high-temperature deformation; aluminum matrix composite; superplastic deformation;
D O I
10.1016/S0924-0136(96)02653-2
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The high temperature deformation of 2124/SiCp (17 vol.%) Composite material was investigated over the temperature range from 698 K to 823 K. It was shown that the 2124/SiCp composite did not behave superplastically at strain rates of from 10(-4) to 10(-1) s(-1). The strain rate sensitivity was found to be about 0.17, which was apparently below that (0.5) of a superplastic material. The activation energy for high temperature deformation was much greater than that of superplastic aluminum alloys. Numerous cavities on the fracture surfaces of the composite were observed by SEM. The high-temperature deformation of the composite was compared with superplastic behavior of 8090/SiCp composite, and the reasons for the 2124/SiCp composite not showing superplastic properties were explained according to superplastic deformation mechanism and the composite itself.
引用
收藏
页码:395 / 398
页数:4
相关论文
共 11 条
[1]  
Bird J.E., 1969, QUANTITATIVE RELATIO, P255
[2]  
CHAN KC, 1996, IN PRESS ACTA METALL
[3]   A THEORETICAL-MODEL FOR HIGH-STRAIN-RATE SUPERPLASTIC BEHAVIOR OF PARTICULATE-REINFORCED METAL-MATRIX COMPOSITES [J].
HAN, BQ ;
CHAN, KC ;
YUE, TM ;
LAU, WS .
SCRIPTA METALLURGICA ET MATERIALIA, 1995, 33 (06) :925-930
[4]  
HAN BQ, 1995, P 10 INT C COMP MAT, V2, P91
[5]   SUPERPLASTICITY IN beta-SILICON NITRIDE WHISKER-REINFORCED 2124 ALUMINIUM COMPOSITE [J].
IMAI, T ;
MABUCHI, M ;
TOZAWA, Y ;
YAMADA, M .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1990, 9 (03) :255-257
[6]   HIGH-TEMPERATURE DEFORMATION-BEHAVIOR OF 20 VOL-PERCENT SICW/2024AL METAL-MATRIX COMPOSITE [J].
KIM, HY ;
HONG, SH .
SCRIPTA METALLURGICA ET MATERIALIA, 1994, 30 (03) :297-302
[7]   AN INVESTIGATION OF THE ROLE OF A LIQUID-PHASE IN AL-CU-MG METAL-MATRIX COMPOSITES EXHIBITING HIGH-STRAIN RATE SUPERPLASTICITY [J].
MABUCHI, M ;
HIGASHI, K ;
LANGDON, TG .
ACTA METALLURGICA ET MATERIALIA, 1994, 42 (05) :1739-1745
[8]   SUPERPLASTIC-LIKE BEHAVIOR IN AS-EXTRUDED AL-ZN-MG ALLOY MATRIX COMPOSITES REINFORCED WITH SI3N4 WHISKERS [J].
MABUCHI, M ;
HIGASHI, K ;
TANIMURA, S ;
IMAI, T ;
KUBO, K .
SCRIPTA METALLURGICA ET MATERIALIA, 1991, 25 (07) :1675-1680
[9]  
MABUCHI M, 1994, SCRIPTA METALL MAT, V30, P297
[10]   SUPERPLASTICITY AT HIGH-STRAIN RATES IN A SIC WHISKER REINFORCED AL-ALLOY [J].
NIEH, TG ;
HENSHALL, CA ;
WADSWORTH, J .
SCRIPTA METALLURGICA, 1984, 18 (12) :1405-1408