Formation of Alumina Layer on Fe-Cr-Ni Alloy by Pack Cementation and Oxidation

被引：2
作者：
Xing, Linlin [1 ]
Zheng, Yanjun [1 ]
Cui, Lishan [1 ]
Sun, Maohu [1 ]
Shao, Mingzeng [1 ]
Lu, Guiwu [1 ]
机构：
[1] China Univ Petr, Dept Mat Sci & Engn, Beijing 102249, Peoples R China
来源：
HIGH TEMPERATURE MATERIALS AND PROCESSES | 2011年 / 30卷 / 1-2期
关键词：
High temperature alloy; coke deposition; oxidation; pack cementation; HIGH-TEMPERATURE OXIDATION; EARLY-STAGE; BEHAVIOR; VAPOR; CARBURIZATION; COATINGS; NI3AL;
D O I：
10.1515/HTMP.2011.013
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
To protect Fe-Cr-Ni based alloy from high temperature corrosion in carbon containing atmosphere at elevated temperature, alumina coating was prepared on the Fe-Ni-Cr alloy substrate by pack cementation and oxidation. Results showed that a surface FeAl layer formed after the pack cementation process, and an Al2O3 coating formed by selective oxidation of the FeAl layer. The coating adhered tightly to the FeAl layer without any cracks or porous inbetween them. By the oxidation process the catalytic elements such as Fe and Ni were remarkably reduced from the surface. Further anti-coking test indicated that the alumina scale could successfully inhibit the outward diffusion of catalytic elements and showed excellent coking resistance.
引用
收藏
页码：99 / 103
页数：5
相关论文
共 21 条
  • [1] Steam oxidation resistant coatings for steam turbine components:: A feasibility study
    Agüero, A
    de Blas, JG
    Muelas, R
    Sanchez, A
    Tsipas, S
    [J]. HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 : 939 - 946
  • [2] BAYER GT, 1995, MATER PERFORMANCE, V34, P34
  • [3] Temperature dependence of metastable alumina formation during thermal oxidation of FeCrAl foils
    Berthomé, G
    N'Dah, E
    Wouters, Y
    Galerie, A
    [J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2005, 56 (06): : 389 - 392
  • [4] CHEVALIER S, 2005, P 6 INT C MICR OX BI, P365
  • [5] Water vapor effect on high-temperature oxidation behavior of Fe3Al intermetallics
    Chevalier, Sebastian
    Juzon, Pitor
    Przybylski, Kazimierz
    Larpin, Jean-Pierre
    [J]. SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2009, 10 (04)
  • [6] The influence of dimethyl disulfide on naphtha steam cracking
    Dhuyvetter, I
    Reyniers, MF
    Froment, GF
    Marin, GB
    Viennet, D
    [J]. INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2001, 40 (20) : 4353 - 4362
  • [7] Oxidation behavior of Ni3Al and FeAl intermetallics under low oxygen partial pressures
    Gao, W
    Li, ZW
    Wu, Z
    Li, S
    He, YD
    [J]. INTERMETALLICS, 2002, 10 (03) : 263 - 270
  • [8] HIGH-TEMPERATURE OXIDATION OF FE-13CR-XAL ALLOYS IN AIR-H2O VAPOR MIXTURES
    KVERNES, I
    OLIVEIRA, M
    KOFSTAD, P
    [J]. CORROSION SCIENCE, 1977, 17 (03) : 237 - 252
  • [9] Carburization behaviour of Mn-Cr-O spinel in high temperature hydrocarbon cracking environment
    Li, Hao
    Zheng, Yanjun
    Benum, Leslie W.
    Oballa, Mike
    Chen, Weixing
    [J]. CORROSION SCIENCE, 2009, 51 (10) : 2336 - 2341
  • [10] LI M, 2009, THESIS CHINA U PETRO
123