Mechanical properties of Cr-O-N coatings deposited by cathodic arc evaporation

被引：36
|
作者：
Warcholinski, B. [1 ]
Gilewicz, A. [1 ]
Kuprin, A. S. [2 ]
Tolmachova, G. N. [2 ]
Ovcharenko, V. D. [2 ]
Kuznetsova, T. A. [3 ]
Zubar, T., I [3 ]
Khudoley, A. L. [3 ]
Chizhik, S. A. [3 ]
机构：
[1] Koszalin Univ Technol, Fac Technol & Educ, Koszalin, Poland
[2] Natl Sci Ctr Kharkov Inst Phys & Technol, Kharkov, Ukraine
[3] Natl Acad Sci Belarus, AV Luikov Heat & Mass Transfer Inst, Minsk, BELARUS
来源：
VACUUM | 2018年 / 156卷
关键词：
Cr-O-N; Arc deposition; AFM; Hardness; Adhesion; Wear; CRYSTAL-CHEMICAL APPROACH; SUBSTRATE BIAS VOLTAGE; OXYNITRIDE THIN-FILMS; OXYGEN-CONTENT; HARD COATINGS; TRIBOLOGICAL BEHAVIORS; OXIDATION RESISTANCE; DROPLET FORMATION; MICROSTRUCTURE; STEEL;
D O I：
10.1016/j.vacuum.2018.07.017
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Ternary chromium based coatings (Cr-O-N) were formed on HS6-5-2 steel substrates using a vacuum arc plasma flux coating system at different relative oxygen concentrations, O-2(x) = O-2/(N-2 + O-2). The mechanical and tribological properties of the coatings were characterized using scanning electron microscopy (SEM), atomic force microscopy (AFM), hardness measurements, wear test and adhesion tests (scratch test and Daimler-Benz test). Special attention was paid to coating adhesion and failure modes in the adhesion tests. The coefficient of friction, wear rate and adhesion decreased as the relative oxygen concentration increased. Hardness of the coatings showed the opposite effect, increasing from approximately 19 GPa-30 GPa. The dominant failure mode of Cr-O-N coatings was abrasion. Individual micro fragmentation was also observed for Cr-O-N coating with O-2(x) = 20%.
引用
收藏
页码：97 / 107
页数：11
相关论文
共 50 条
  • [21] Influence of boron ion implantaton on the mechanical properties of tin coatings deposited by cathodic arc evaporation
    Zhu, YC
    Matsumoto, Y
    Fujita, K
    Iwamoto, N
    Nagasaka, N
    Kataoka, T
    SURFACE ENGINEERING: IN MATERIALS SCIENCE I, 2000, : 423 - 431
  • [22] Comparison on the structural, mechanical and tribological properties of TiAlN coatings deposited by HiPIMS and Cathodic Arc Evaporation
    Alhafian, M.-R.
    Chemin, J.-B.
    Fleming, Y.
    Bourgeois, L.
    Penoy, M.
    Useldinger, R.
    Soldera, F.
    Mücklich, F.
    Choquet, P.
    Surface and Coatings Technology, 2021, 423
  • [23] Structure and Properties of AlCrN Coatings Deposited Using Cathodic Arc Evaporation
    Warcholinski, Bogdan
    Gilewicz, Adam
    Myslinski, Piotr
    Dobruchowska, Ewa
    Murzynski, Dawid
    COATINGS, 2020, 10 (08)
  • [24] EFFECT OF NITROGEN PRESSURE ON THE STRUCTURAL AND MECHANICAL PROPERTIES OF V-Mo-N COATINGS DEPOSITED BY CATHODIC ARC EVAPORATION
    Kuprin, A. S.
    Reshetnyak, E. N.
    Gilewicz, A.
    Warcholinski, B.
    Vasilenko, R. L.
    Rostova, H. Yu.
    Klimenko, I. O.
    Tolmachova, G. N.
    Ilchenko, A. V.
    PROBLEMS OF ATOMIC SCIENCE AND TECHNOLOGY, 2022, (04): : 107 - 113
  • [25] Effect of a Gas Medium on the Mechanical, Tribological, and Anticorrosion Properties of Cr–Ni–Al–C–N Coatings Deposited by the Pulsed Cathodic Arc Evaporation Method
    Ph. V. Kiryukhantsev-Korneev
    A. D. Sytchenko
    A. N. Sheveyko
    V. A. Gorshkov
    E. A. Levashov
    Physics of Metals and Metallography, 2021, 122 : 1241 - 1247
  • [26] Oxygen effect on the mechanical behaviors of Cr(N,O)/CrN double-layered coatings by cathodic arc evaporation
    Ho, WY
    Hsu, CH
    Huang, DH
    Cheng, YP
    Lin, YC
    Chang, CL
    SURFACE & COATINGS TECHNOLOGY, 2004, 188 : 129 - 134
  • [27] NiCoCrAlYTa coatings deposited by the cathodic arc evaporation technique
    Damond, E.
    Jacquot, P.
    Denisse, E.
    Vide, les Couches Minces, 1992, (261):
  • [28] The Effect of Substrate Duty Cycle on the Mechanical and Electrochemical Properties of TiAlN Coatings Deposited by Cathodic Arc Evaporation
    Mohammadi, Majid
    Toloueipour, Mina
    Yazdani, Arash
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
  • [29] Plasma analyses and structural properties of Cr-N-C-O coatings synthesized by a cathodic arc evaporation process
    Chang, Yin-Yu
    Yang, Shun-Jan
    Wu, Weite
    THIN SOLID FILMS, 2009, 517 (14) : 4238 - 4241
  • [30] Effect of bias voltage on microstructure, mechanical and wear properties of Al-Si-N coatings deposited by cathodic arc evaporation
    Chang, Chi-Lung
    Huang, Chi-Song
    THIN SOLID FILMS, 2011, 519 (15) : 4923 - 4927
12345