Effect of cristobalite formation on the delamination resistance of an oxide/Si/(SiC/SiC) environmental barrier coating system after cyclic high temperature thermal exposure

被引:51
作者
Arai, Yutaro [1 ]
Aoki, Yuto [1 ]
Kagawa, Yutaka [1 ]
机构
[1] Tokyo Univ Technol, Katayanagi Adv Res Labs, 1404-1 Katakura, Hachioji, Tokyo 1920982, Japan
关键词
Environmental barrier coating; Delamination toughness; Cristobalite; Cyclic thermal exposure; SiC/SiC; WATER-VAPOR; COMPOSITES;
D O I
10.1016/j.scriptamat.2017.06.006
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Delamination toughness of a mullite/Si/(SiC/SiC) environmental barrier coating (EBC) system has been measured using a shear-loading test. The EBC system is initially heated to a temperature of 1470 degrees C (above the melting point of Si (1414 degrees C)), and then repeated thermal exposure is carried out at a temperature 1320 degrees C (below the melting point of Si) for 2 h/cycle. Change of the delamination toughness with heat exposure is successfully obtained using the shear-loading test. Formation of cristobalite and transformation from a alpha-beta during thermal cycling cause an increase of crack density in the Si bond coat layer and a resulting reduction in delamination toughness. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码:58 / 62
页数:5
相关论文
共 27 条
[1]   EFFECT OF STATIC UNIAXIAL STRESS ON RAMAN SPECTRUM OF SILICON [J].
ANASTASSAKIS, E ;
PINCZUK, A ;
BURSTEIN, E ;
POLLAK, FH ;
CARDONA, M .
SOLID STATE COMMUNICATIONS, 1970, 8 (02) :133-+
[2]   A simple method for measurement of shear delamination toughness in environmental barrier coatings [J].
Aoki, Yuto ;
Inoue, Junya ;
Kagawa, Yutaka ;
Igashira, Kenichiroh .
SURFACE & COATINGS TECHNOLOGY, 2017, 321 :213-218
[3]   RAMAN SPECTRA OF ALPHA-CRISTOBALITE AND BETA-CRISTOBALITE [J].
BATES, JB .
JOURNAL OF CHEMICAL PHYSICS, 1972, 57 (09) :4042-+
[4]  
Caradarelli F., 2000, MAT HDB, P339
[5]   Elastic Modulus Evolution and Behavior of Si/Mullite/BSAS-Based Environmental Barrier Coatings Exposed to High Temperature in Water Vapor Environment [J].
Cojocaru, C. V. ;
Kruger, S. E. ;
Moreau, C. ;
Lima, R. S. .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2011, 20 (1-2) :92-99
[6]  
DiCarlo JA, 2015, CERAMIC MATRIX COMPOSITES: MATERIALS, MODELING AND TECHNOLOGY, P217
[7]   Accelerated oxidation of SiCCMC's by water vapor and protection via environmental barrier coating approach [J].
Eaton, HE ;
Linsey, GD .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (14-15) :2741-2747
[8]  
Hridenreich B., 2015, CERAMIC MATRIX COMPO, P147
[9]   Lifetime Assessment for Thermal Barrier Coatings: Tests for Measuring Mixed Mode Delamination Toughness [J].
Hutchinson, Robert G. ;
Hutchinson, John W. .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 :S85-S95
[10]  
Kagawa Y, 2017, J GAS TURBINE UNPUB