Barrier and self-healing abilities of corrosion protective polymer coatings and metal powders for aluminum alloys

被引：24
作者：
Yabuki, A.
Yamagami, H.
Noishiki, K.
机构：
[1] Hiroshima Univ, Grad Sch Engn, Higashihiroshima 7398527, Japan
[2] Kobe Steel Ltd, Machinery & Engn Co, Takasago, Hyogo 6768670, Japan
来源：
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2007年 / 58卷 / 07期
关键词：
D O I：
10.1002/maco.200604041
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Several types of coatings, designed to improve the resistance of aluminum alloys to corrosion in seawater, were examined. A coating with a thickness of approximately 30 mu m was applied to the surface of aluminum alloy 3003, and after creating an artificial defect by means of a knife-edge, a corrosion test was carried out in 3% NaCl solution at a temperature of 70 degrees C and pH 1.5. The test results showed that a fluorine resin and sol-gel coatings both had excellent barrier abilities. The fluorine resin coating had self-healing abilities, and this was improved by the addition of a metal powder.
引用
收藏
页码：497 / 501
页数：5
相关论文
共 21 条
[1]   Self-healing protective films prepared on zinc electrodes by treatment in a cerium(III) nitrate solution and modification with sodium phosphate and calcium or magnesium nitrate [J].
Aramaki, K .
CORROSION SCIENCE, 2003, 45 (10) :2361-2376
[2]   Self-healing protective films prepared on zinc by treatments with cerium(III) nitrate and sodium phosphate [J].
Aramaki, K .
CORROSION SCIENCE, 2002, 44 (11) :2621-2634
[3]   Self-healing mechanism of an organosiloxane polymer film containing sodium silicate and cerium(III) nitrate for corrosion of scratched zinc surface in 0.5 M NaCl [J].
Aramaki, K .
CORROSION SCIENCE, 2002, 44 (07) :1621-1632
[4]   Preparation of chromate-free, self-healing polymer films containing sodium silicate on zinc pretreated in a cerium(III) nitrate solution for preventing zinc corrosion at scratches in 0.5 M NaCl [J].
Aramaki, K .
CORROSION SCIENCE, 2002, 44 (06) :1375-1389
[5]   Improvement in the self-healing ability of a protective film consisting of hydrated cerium(III) oxide and sodium phosphate layers on zinc [J].
Aramaki, K .
CORROSION SCIENCE, 2003, 45 (02) :451-464
[6]   XPS and EPMA studies on self-healing mechanism of a protective film composed of hydrated cerium(III) oxide and sodium phosphate on zinc [J].
Aramaki, K .
CORROSION SCIENCE, 2003, 45 (01) :199-210
[7]   Preparation of self-healing protective films on a zinc electrode treated in a cerium(III) nitrate solution and modified with sodium phosphate and cerium(III) nitrate [J].
Aramaki, K .
CORROSION SCIENCE, 2004, 46 (06) :1565-1579
[8]   Self-healing mechanism of a protective film prepared on a Ce(NO3)3-pretreated zinc electrode by modification with Zn(NO3)2 and Na3PO4 [J].
Aramaki, K .
CORROSION SCIENCE, 2003, 45 (05) :1085-1101
[9]   EIS of cathodically deposited wet paint films prior to the stoving process [J].
Beck, F ;
Kruger, UA .
ELECTROCHIMICA ACTA, 1996, 41 (7-8) :1083-1092
[10]   STRUCTURE-PROPERTY RELATIONSHIPS IN THIN-FILMS AND MEMBRANES [J].
BRINKER, CJ ;
RAMAN, NK ;
LOGAN, MN ;
SEHGAL, R ;
ASSINK, RA ;
HUA, DW ;
WARD, TL .
JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 1995, 4 (02) :117-133
123