Rheological Properties of Polymer Melts with High Elasticity

In the recent years efforts to complex description of the rheological characteristic increase even in the case of polymeric blends with high part of elastic deformation. However, unlike the most thermoplastic these blends have a certain specific features. Besides the already mentioned the higher part of elastic deformation it is especially higher viscosity, which are shown mainly for the measurement in the range of high shear rates. For this reason, the presented work is focused on the description of measurement methodology for blends with high part of elastic deformation using capillary rheometer. The measurements were carried out on a commercial polymer blend with trade name A517 based on rubbery polymer. Capillary rheometer Gottfert RG 75 was used, with diameter of chamber 15 mm. Measurements were performed using capillaries with different ratio of length/diameter at temperature 100 degrees C. Because of existence elastic part of deformation, it is not possible to achieve a steady state pressure using measurements at constant volumetric flow at high shear rates. Therefore we decided to measure the flow characteristic using isobaric mode.