Gas sensing properties of nanocrystalline tungsten oxide synthesized by acid precipitation method

被引：30

作者：

Senguttuvan, T. D. ^{[1
]}

Srivastava, Vibha ^{[1
]}

Tawal, Jai S. ^{[2
]}

Mishra, Monika ^{[1
]}

Srivastava, Shubhda ^{[1
]}

Jain, Kiran ^{[1
]}

机构：

[1] Natl Phys Lab, Elect Mat Div, New Delhi 110012, India

[2] Natl Phys Lab, Mat Characterizat Div, New Delhi 110012, India

来源：

SENSORS AND ACTUATORS B-CHEMICAL | 2010年 / 150卷 / 01期

关键词：

WO3; Metal oxide; Gas sensor; Ammonia sensor; Thick film; Chemical synthesis; WO3; THIN-FILMS; MICROSTRUCTURE; SENSOR; SIZE; NOX;

D O I：

10.1016/j.snb.2010.06.053

中图分类号：

O65 [分析化学];

学科分类号：

070302 ; 081704 ;

摘要：

WO3 2H(2)O samples were prepared by acidic precipitation of sodium tungstate solution Nanocrystalline WO3 powders were obtained after 350 and 600 degrees C calcinations. XRD patterns of these samples showed a diffraction profile similar to that of monoclinic WO3 Calcinations at 600 degrees C yield WO3 powders with particle sizes ranging (loin 60 to 170 nm whereas that for 350 degrees C calculations ale in the range of 30-150 nm The gas sensing properties of these powders in the form of thick film were investigated with and without platinum doping Gas response of thick films sintered at two different temperatures was measured at four different operating temperatures We confirm that the sensor elements made from 600 degrees C calcined powders doped with platinum sintered at 800 degrees C ate highly responsive and selective to ammonia vapour at 350 degrees C operating temperature as compared to sensor elements made from commercial powders (C) 2010 Elsevier B.V. All rights reserved

引用

页码：384 / 388

页数：5

共 20 条

[11] Metal oxides for solid-state gas sensors: What determines our choice?
Korotcenkov, G.
[J]. MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2007, 139 (01): : 1 - 23
[12] Influence of annealing on microstructure and NO2-sensing properties of sputtered WO3 thin films
Liu, Zhifu
Yamazaki, Toshinai
Shen, Yanbai
Kikuta, Toshio
Nakatani, Noriyuki
[J]. SENSORS AND ACTUATORS B-CHEMICAL, 2007, 128 (01) : 173 - 178
[13] A semiconducting metal oxide sensor array for the detection of NOx and NH3
Marquis, BT
Vetelino, JF
[J]. SENSORS AND ACTUATORS B-CHEMICAL, 2001, 77 (1-2) : 100 - 110
[14] Stoichiometry and microstructure effects on tungsten oxide chemiresistive films
Moulzolf, SC
Ding, SA
Lad, RJ
[J]. SENSORS AND ACTUATORS B-CHEMICAL, 2001, 77 (1-2) : 375 - 382
[15] NOx gas sensing characteristics of WO3 thin films activated by noble metals (Pd, Pt, Au) layers
Penza, M
Martucci, C
Cassano, G
[J]. SENSORS AND ACTUATORS B-CHEMICAL, 1998, 50 (01) : 52 - 59
[16] Nanocrystalline tungsten oxide thick-films with high sensitivity to H2S at room temperature
Solis, JL
Saukko, S
Kish, LB
Granqvist, CG
Lantto, V
[J]. SENSORS AND ACTUATORS B-CHEMICAL, 2001, 77 (1-2) : 316 - 321
[17] Highly sensitive NH3 sensor using Pt catalyzed silica coating over WO3 thick films
Srivastava, Vibha
Jain, Kiran
[J]. SENSORS AND ACTUATORS B-CHEMICAL, 2008, 133 (01) : 46 - 52
[18] Nanocrystalline tungsten oxide thin film: Preparation, microstructure, and photochromic behavior
Sun, M
Xu, N
Cao, YW
Yao, JN
Wang, EG
[J]. JOURNAL OF MATERIALS RESEARCH, 2000, 15 (04) : 927 - 933
[19] GRAIN-SIZE EFFECTS IN TUNGSTEN OXIDE-BASED SENSOR FOR NITROGEN-OXIDES
TAMAKI, J
ZHANG, Z
FUJIMORI, K
AKIYAMA, M
HARADA, T
MIURA, N
YAMAZOE, N
[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1994, 141 (08) : 2207 - 2210
[20] Wang YD, 2001, SOLID STATE ELECTRON, V45, P639, DOI 10.1016/S0038-1101(01)00126-5

← 1 2 →