A low-temperature solution-processed indium incorporated zinc oxide electron transport layer for high-efficiency lead sulfide colloidal quantum dot solar cells

Colloidal quantum dot solar cells (CQDSCs) have achieved remarkable progress recently in terms of mainly surface passivation and composition-matching matrices on CQDs, while improving the overall photoelectric conversion efficiency (PCE) through electron transport layer (ETL) modifications is less explored. We report a low-temperature solution route to synthesize donor (Al3+/Ga3+/In3+) incorporated zinc oxide (AZO/GZO/IZO) ETL films for PbS CQDSCs. Spectroscopic characterization studies indicate that the IZO ETL fabricated with 150 degrees C annealing can increase the bandgap the most from 3.56 eV to 3.74 eV, possesses enhanced light transmission (similar to 94%) and finer particle sizes, and importantly shows the most suitable band alignment and charge transfer ability. Well-dispersed PbS CQDs of around 3 nm are synthesized by a N-2-protected reflux method and are surface exchanged with 1-ethyl-3-methylimidazolium iodide (EMII) to allow I-grafting and ethanedithiol (EDT) for the active layer and hole transport layer, respectively. The IZO based PbS CQDSC, with a device architecture of ITO/IZO/PbS-EMII/ PbS-EDT/Au, shows an enhanced PCE of 11.1% (comparatively 18% higher than that of the ZnO ETL), a V-OC value of 0.64 V, and a J(SC) of 25.8 mA cm(-2). The improved performances benefit from the higher recombination resistance and constrained photoluminescence emission with the utilization of the IZO ETL that provides a superior charge transfer property.