The effect of single overloads in tension and compression on the fatigue crack propagation behaviour of short cracks

被引：17
|
作者：
Zhou, Xiang [1 ,2 ]
Gaenser, Hans-Peter [1 ]
Pippan, Reinhard [2 ,3 ]
机构：
[1] Mat Ctr Leoben Forsch GmbH, Roseggerstr 12, A-8700 Leoben, Austria
[2] Austrian Acad Sci, Erich Schmid Inst Mat Sci, Jahnstr 12, A-8700 Leoben, Austria
[3] Univ Leoben, Dept Mat Phys, Jahnstr 12, A-8700 Leoben, Austria
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2016年 / 89卷
关键词：
Overload; Crack closure; Residual stress; Threshold of stress intensity; Effective threshold; FINITE-ELEMENT ANALYSIS; GROWTH; CLOSURE; THRESHOLD; METALS; STEEL;
D O I：
10.1016/j.ijfatigue.2016.02.001
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The crack propagation behaviour in cast quenched and tempered steel after one overload cycle in tension as well as in compression on short cracks is investigated in deep notched specimens. The overload cycle exhibits a significant influence on the fatigue life endurance, due to the formation of an overload plastic zones in front of the crack tip. The crack propagation after overload cycles is investigated by inspection of the fatigue threshold R-curve and fatigue crack propagation rate. Tension overload increased the long crack threshold and reduced the R-curve effect, whereas overloads in compression reduced the crack growth resistance and shifted the threshold value to larger crack extension. A simple FE simulation was also performed to investigate the variation in the contribution of plasticity induced crack closure during crack propagation after the overload. Macroscopic mechanistic and dislocation models are introduced to explain the results obtained. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：77 / 86
页数：10
相关论文
共 50 条
  • [31] Fatigue notch factor and short crack propagation
    Verreman, Yves
    Limodin, Nathalie
    ENGINEERING FRACTURE MECHANICS, 2008, 75 (06) : 1320 - 1335
  • [32] Deformation behaviour at the tip of a physically short fatigue crack due to a single overload
    Hammouda, MMI
    Ahmad, SSE
    Sherbini, AS
    Sallam, HEM
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1999, 22 (02) : 145 - 151
  • [33] Propagation of physically short cracks in a bainitic high strength bearing steel due to fatigue load
    Alfredsson, B.
    Oberg, M.
    Lai, J.
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 90 : 166 - 180
  • [34] Effect of Solution Annealing on Fatigue Crack Propagation in the AISI 304L TRIP Steel
    Jambor, Michal
    Vojtek, Tomas
    Pokorny, Pavel
    Smid, Miroslav
    MATERIALS, 2021, 14 (06)
  • [35] Fatigue crack propagation behaviour of a nickel based superalloy at elevated temperatures
    Wang, L.
    Huang, X.
    Guo, G.
    Hu, Y.
    Zhang, L.
    MATERIALS RESEARCH INNOVATIONS, 2014, 18 : 1087 - 1090
  • [36] Fatigue crack propagation behaviour of steels with different microstructures
    Xu, Tianhan
    Feng, Yaorong
    Song, Shengyin
    Wang, Danghui
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 551 : 110 - 115
  • [37] EFFECT OF CONSTRAINT ON FATIGUE CRACK PROPAGATION IN NOTCHED PLATES
    Wang, Xin
    PROCEEDINGS OF THE ASME 29TH INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, 2010, VOL 6, 2010, : 213 - 217
  • [38] A study of overload effect on fatigue crack propagation using EBSD, FIB-DIC and FEM methods
    Salvati, E.
    O'Connor, S.
    Sui, T.
    Nowell, D.
    Korsunsky, A. M.
    ENGINEERING FRACTURE MECHANICS, 2016, 167 : 210 - 223
  • [39] Physically short crack propagation in metals during high cycle fatigue
    Santus, C.
    Taylor, D.
    INTERNATIONAL JOURNAL OF FATIGUE, 2009, 31 (8-9) : 1356 - 1365
  • [40] NUMERICAL ANALYSIS OF OVERLOAD/UNDERLOAD EFFECT ON FATIGUE CRACK PROPAGATION BEHAVIOR OF AH32 STEEL
    Dong Qin
    DaiQiansheng
    XuGeng
    PROCEEDINGS OF ASME 2024 43RD INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, OMAE2024, VOL 2, 2024,
12345