Effect of Melt Conditioning on Removal of Fe from Secondary Al-Si Alloys Containing Mg, Mn, and Cr

被引:26
作者
Becker, Hanka [1 ]
Thum, Angela [1 ]
Distl, Benedikt [1 ]
Kriegel, Mario J. [1 ]
Leineweber, Andreas [1 ]
机构
[1] TU Bergakad Freiberg, Inst Mat Sci, Gustav Zeuner Str 5, D-09599 Freiberg, Germany
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2018年 / 49A卷 / 12期
关键词
CONTAINING INTERMETALLIC PHASES; CRYSTAL-STRUCTURE; THERMODYNAMIC ASSESSMENT; BETA-AL5FESI PHASE; RECYCLED ALUMINUM; SILICON ALLOYS; ALFESI PHASE; COOLING RATE; IRON; SYSTEM;
D O I
10.1007/s11661-018-4930-7
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Primary intermetallic sludge formation in hypoeutectic secondary Al7.1Si(1.5-x(M))Fex(M)M alloys was investigated in view of potential Fe removal by separation of sludge and Al melt. M is Mg, Mn, and Cr, with Mg as typical alloying element and Mn and Cr as additions to modify the sludge. Differential thermal analysis was used to determine the onset temperatures of sludge formation and solidification of the (Al)-solid solution. These temperatures were compared with results from the semi-empirical sludge factor approach and thermodynamic calculations. The chosen conditioning temperature of 620 degrees C is slightly above the onset temperature of solidification of the (Al)-solid solution in all alloys. At 620 degrees C, sludge did not form in alloys with x(Mg)0.6at.pct. In all other alloys, sludge has formed. In the ternary Al7.1Si1.5Fe alloy and the alloy with x(Mg)=0.3at.pct, the hexagonal (h) phase is responsible for binding Fe, whereas Mg remains in the melt. The cubic (c) phase binds Fe from the melt of Mn- and Cr-containing alloys. The (Al,Si)(2)Cr and Al13Cr4Si4 phases additionally bind Cr. The potential separation of the sludge from the residual melt leads to relative Fe removal up to 67pct and relative transition-metal removal up to 65 and 83pct.
引用
收藏
页码:6375 / 6389
页数:15
相关论文
共 84 条
[1]   THERMO-CALC & DICTRA, computational tools for materials science [J].
Andersson, JO ;
Helander, T ;
Höglund, LH ;
Shi, PF ;
Sundman, B .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2002, 26 (02) :273-312
[2]   Removal of iron from recycled aluminium alloys [J].
Ashtari, P. ;
Tetley-Gerard, K. ;
Sadayappan, K. .
CANADIAN METALLURGICAL QUARTERLY, 2012, 51 (01) :75-80
[3]   Thermodynamic assessment of the quaternary system Al-Fe-Mn-Si in the Al-rich corner [J].
Balitchev, E ;
Jantzen, T ;
Hurtado, I ;
Neuschütz, D .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2003, 27 (03) :275-278
[4]   Approximate icosahedral symmetry of α-Al(Fe,Mn,Cr)Si in electron backscatter diffraction analysis of a secondary Al-Si casting alloy [J].
Becker, Hanka ;
Leineweber, Andreas .
MATERIALS CHARACTERIZATION, 2018, 141 :406-411
[5]  
Belov NA, 2005, MULTICOMPONENT PHASE DIAGRAMS: APPLICATIONS FOR COMMERCIAL ALUMINUM ALLOYS, pV, DOI 10.1016/B978-008044537-3/50000-7
[6]   In-situ study of morphology and growth of primary α-Al(FeMnCr)Si intermetallics in an Al-Si alloy [J].
Bjurenstedt, Anton ;
Casari, Daniele ;
Seifeddine, Salem ;
Mathiesen, Ragnvald H. ;
Dahle, Arne K. .
ACTA MATERIALIA, 2017, 130 :1-9
[7]   The Effects of Fe-Particles on the Tensile Properties of Al-Si-Cu Alloys [J].
Bjurenstedt, Anton ;
Seifeddine, Salem ;
Jarfors, Anders E. W. .
METALS, 2016, 6 (12)
[8]   Crystal structure of the monoclinic β-Al11Cr2 [J].
Cao, B. B. ;
Kuo, K. H. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 458 (1-2) :238-247
[9]   The nucleation of Fe-rich phases on oxide films in Al-11.5Si-0.4Mg cast alloys [J].
Cao, X ;
Campbell, J .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (07) :1409-1420
[10]   Morphology of β-Al5FeSi phase in Al-Si cast alloys [J].
Cao, Xinjin ;
Campbell, John .
MATERIALS TRANSACTIONS, 2006, 47 (05) :1303-1312