WELDABILITY STUDIES of HIGH-Cr, Ni-BASE filler metals for power generation applications

被引:42
作者
Alexandrov, B. T. [1 ]
Hope, A. T. [1 ]
Sowards, J. W. [2 ]
Lippold, J. C. [1 ]
McCracken, S. [3 ]
机构
[1] Ohio State Univ, Welding Engn Program, Columbus, OH 43210 USA
[2] OSU, NIST, Boulder, CO USA
[3] Elect Power Res Inst, Charlotte, NC USA
关键词
Chromium; Cracking; High alloy steels; Nickel alloys; Filler materials; Solidification; Weld metal; Weldability tests; DUCTILITY-DIP CRACKING; HIGH-TEMPERATURE BEHAVIOR; WELD METAL; SUSCEPTIBILITY; MECHANISM;
D O I
10.1007/BF03321288
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The solidification behaviour and weld solidification cracking susceptibility of high-Cr, Ni-base filler metals that are widely used, or proposed for use, in the nuclear power industry have been investigated. Two heats of ERNiCrFe-13 (filler metal 52MSS), one heat of ERNiCrFe-7A (filler metal 52M), and one heat of a modified ERNiCr-3 (filler metal 82 with higher Cr content, designated here as filler metal 52i) have been tested using both the Transvarestraint test and the Cast Pin Tear test (CPU). The solidification behaviour in these alloys has been studied by a newly developed procedure that accurately replicates the solidification process in fusion welds of Ni-base alloys and is based on the patented technique for Single Sensor Differential Thermal Analysis (SS DTA (TM)). Results of the solidification studies showed that filler metal 52i has the widest solidification range, followed by the two heats of filler metal 52MSS, and filler metal 52M. The filler metal 52i also has the widest eutectic temperature range. The interdendritic eutectic constituent formed in weld metal of this filler metal and filler metal 52MSS is enriched in Nb and results from the eutectic reaction of gamma + L -> gamma + NbC at the end of solidification. Both the CPU and the Transvarestraint test provided the same ranking of solidification cracking susceptibility among these filler metals. Both heats of 52MSS and the heat of 52i were found to be more susceptible to solidification cracking than filler metal 52M. The slightly higher resistance to solidification cracking of filler metal 52i relative to the 52MSS filler metals is attributed to crack "healing" during the final stages of solidification. This is the result of the higher fraction of eutectic liquid of filler metal 52i, as confirmed by metallographic studies. The results of this study confirm the higher solidification cracking susceptibility of high-Cr, Ni-base filler metals that contain higher Nb levels to counteract ductility-dip cracking, relative to filler metals that are Nb-free. This study has also shown that the CPU can be used as an alternative, and reliable, tool for ranking the solidification cracking susceptibility of high-Cr, Ni-base filler metals proposed for use in nuclear power plants and other applications.
引用
收藏
页码:65 / 76
页数:12
相关论文
共 19 条
[1]  
Alexandrov B. T., 2008, 8 INT TRENDS WELD RE
[2]  
ALEXANDROV BT, 2008, P HOT CRACKING PHENO, V2, P193
[3]  
Alexandroy B T, 2009, Method and device for investigation of phasetransformations in metals and alloys United States, Patent No. [US 7,473,028 B1, 7473028]
[4]  
Dupont JN, 1998, WELD J, V77, p417S
[5]   Solidification of Nb-bearing superalloys: Part I. Reaction sequences [J].
DuPont, JN ;
Robino, CV ;
Michael, JR ;
Notis, MR ;
Marder, AR .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (11) :2785-2796
[6]   Solidification of Nb-bearing superalloys: Part II. Pseudoternary solidification surfaces [J].
DuPont, JN ;
Robino, CV ;
Marder, AR ;
Notis, MR .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (11) :2797-2806
[7]  
*EL POW RES I, 2008, MRP169 EL POW RES I
[8]  
Electric Power Research Institute, 2004, MRP115 EL POW RES I
[9]  
*EPRI NP, 1991, EPRINP7085D
[10]  
FINTON TL, 2004, SR0402 EWI