Effect of nanocrystallization on tribological behaviors of ingot iron

被引：32

作者：

Lv, X. R. ^{[1
]}

Wang, S. G. ^{[1
,2
]}

Liu, Y. ^{[1
]}

Long, K. ^{[1
]}

Li, S. ^{[1
]}

Zhang, Z. D. ^{[1
,2
]}

机构：

[1] Chinese Acad Sci, Met Res Inst, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China

[2] Chinese Acad Sci, Int Ctr Mat Phys, Shenyang 110016, Peoples R China

来源：

WEAR | 2008年 / 264卷 / 7-8期

基金：

中国国家自然科学基金;

关键词：

severe rolling; nanocrystalline materials; friction; wear;

D O I：

10.1016/j.wear.2007.04.010

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Tribological behaviors of bulk nanocrystalline ingot iron (BNII) resulting from severe rolling with/without annealing have been compared with those of conventional polycrystalline ingot iron (CPII). The results reveal that in dry sliding the wear loss of BNII is higher than that of CPII, although its hardness is significantly enhanced. The wear loss of annealed BNII is the highest due to its lower hardness and the remains of sandwich structure as BNII. In lubricating sliding, the wear loss of BNII is obviously less than that of CPII, while the wear loss of annealed BNII is close to that of CPII. The frictional coefficient of BNII decreases at elevated temperature of the lubricant with additives, but CPII shows the contrary tendency. The reason for variation of tribological behaviors of tested samples is discussed preliminarily. (c) 2007 Elsevier B.V. All rights reserved.

引用

页码：535 / 541

页数：7

共 23 条

[1] Development of nanocrystalline wear-resistant Y-TZP ceramics [J].

Basu, B ;

Lee, JH ;

Kim, DY .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2004, 87 (09) :1771-1774

[2] Pressureless sintering and tribological properties of WC-ZrO2 composites [J].

Basu, B ;

Venkateswaran, T ;

Sarkar, D .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2005, 25 (09) :1603-1610

[3]

EDEMIR A, 1999, SURF COAT TECH, V121, P565

[4] STRAIN-HARDENING OF HIGH-STRENGTH STEELS [J].

GAWNE, DT ;

LEWIS, GMH .

MATERIALS SCIENCE AND TECHNOLOGY, 1985, 1 (02) :128-135

[5] NANOCRYSTALLINE MATERIALS [J].

BIRRINGER, R .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 117 :33-43

[6]

KLUG HP, 1974, XRAY DIFFRACTION PRO, P661

[7] Overview paper no. 2. The synthesis and structure of nanocrystalline materials produced by mechanical attrition. A review [J].

Koch, C.C. .

Nanostructured Materials, 1993, 2 (02)

[8]

Lu K, 1999, J MATER SCI TECHNOL, V15, P193

[9]

LU K, 1991, J APPL PHYS, V69, P252

[10] Effect of grain size on the tribological behavior of nanocrystalline nickel [J].

Mishra, R ;

Basu, B ;

Balasubramaniam, R .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 373 (1-2) :370-373

← 1 2 3 →