Experimental assessment of the representative strains in instrumented sharp indentation

被引：25

作者：

Chollacoop, N ^{[1
]}

Ramamurty, U ^{[1
]}

机构：

[1] Natl Met & Mat Technol Ctr, MTEC, Pathum Thani 12120, Thailand

来源：

SCRIPTA MATERIALIA | 2005年 / 53卷 / 02期

关键词：

microindentation; plastic deformation; tension test; hardness; representative strain;

D O I：

10.1016/j.scriptamat.2005.03.030

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Experimental assessment of the reverse algorithms that enable the extraction of plastic properties from the load-depth of penetration curves was conducted. Results show that they predict the stresses at 3.3% and 5.7% representative strains for Berkovich and 60 degrees cone-equivalent three-sided pyramidal indenters, respectively, with good accuracy. It was shown that the uniaxial stress-strain curves could be reconstructed from the indentation data. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

引用

页码：247 / 251

页数：5

共 8 条

[1] PLASTIC INDENTATION IN METALS WITH CONES [J].

ATKINS, AG ;

TABOR, D .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1965, 13 (03) :149-&

[2] Subsurface strain distribution around Vickers hardness indentations in annealed polycrystalline copper [J].

Chaudhri, MM .

ACTA MATERIALIA, 1998, 46 (09) :3047-3056

[3] Depth-sensing instrumented indentation with dual sharp indenters [J].

Chollacoop, N ;

Dao, M ;

Suresh, S .

ACTA MATERIALIA, 2003, 51 (13) :3713-3729

[4] Computational modeling of the forward and reverse problems in instrumented sharp indentation [J].

Dao, M ;

Chollacoop, N ;

Van Vliet, KJ ;

Venkatesh, TA ;

Suresh, S .

ACTA MATERIALIA, 2001, 49 (19) :3899-3918

[5] ANALYSIS OF VICKERS INDENTATION [J].

GIANNAKOPOULOS, AE ;

LARSSON, PL ;

VESTERGAARD, R .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1994, 31 (19) :2679-2708

[6] CORRELATION OF INDENTATION EXPERIMENTS [J].

JOHNSON, KL .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1970, 18 (02) :115-&

[7]

Johnson KL., 1985, CONTACT MECH

[8]

Tabor D, 1951, HARDNESS METALS, V200

← 1 →