In situ growth of Ca-Zn-P coatings on the Zn-pretreated WE43 Mg alloy to mitigate corrosion and enhance cytocompatibility

Magnesium (Mg) alloys are potential materials for orthopedic fixation devices but rapid degradation of the materials restricts wider clinical applications. Herein, zinc-incorporated calcium phosphate (Ca-Zn-P) coatings are prepared on the Zn-pretreated WE43 Mg alloy by a hydrothermal technique under relatively stable and favorable conditions. The hydrothermal coating consists of a compact bottom layer of CaZn2(PO4)(2)center dot 2 H2O and ZnO granular crystals and a jagged upper layer of CaHPO4. The Zn coating reduces the corrosion current density of WE43 to (3.49 +/- 1.60) x 10(-5) A cm(-2), whereas the Ca-Zn-P/Zn composite coating further reduces it by 3 orders of magnitude in the simulated body fluid (SBF). The charge transfer resistances of the Zn-coated and Ca-Zn-P/Zn-coated alloys increase by 49 and 7176 times to 835 and 1.22 x 10(5) omega cm(2), respectively. The 7-day immersion results reveal that the Zn coating cannot provide long-term protection to WE43 in SBF because of the formation of galvanic couples between the Zn coating and WE43. In contrast, Ca-Zn-P/Zn-coated WE43 remains intact after soaking for 7 days and furthermore, the Ca-Zn-P coating self-repairs and continues to grow despite dissolution. The compact and adherent Ca-Zn-P bottom layer plays a major role in mitigating corrosion of WE43 by hindering penetration of the aggressive medium and charge transfer of the corrosion reactions resulting in only slight corrosion of the Zn layer. Biologically, the Zn coating reduces attachment and proliferation of MC3T3-E1 pre-osteoblasts on WE43, but the composite coating fosters cell adhesion and proliferation which stems from the good biocompatibility of the hydrothermal layer and relatively stable surface conditions avoiding severe corrosion.