Low-temperature ordering of FePt thin films by a thin AuCu underlayer

被引：50

作者：

Zhu, Y ^{[1
]}

Cai, JW ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Phys, State Key Lab Magnet, Beijing 100080, Peoples R China

来源：

APPLIED PHYSICS LETTERS | 2005年 / 87卷 / 03期

基金：

中国国家自然科学基金;

关键词：

D O I：

10.1063/1.1997268

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

We have studied the magnetic and structural properties of AuCu(0-50nm)/FePt(2-50nm) films after annealing at various temperatures. The results indicate that, by introducing a thin equiatomic AuCu underlayer, the ordering temperature of FePt films with thickness even down to 5 nm can be significantly reduced to 350 degrees C, at which a large coercivity is developed. In fact, the coercivity is as high as 4.6 kOe for a 5 nmFePt film on a 10 nm AuCu underlayer after annealing at 350 degrees C and this value is raised up to 7.5 kOe when annealed at 400 degrees C, while the corresponding sample without a AuCu underlayer has to be annealed at a temperature beyond 600 degrees C in order to achieve a coercivity of 4 kOe. The ordering of the thin AuCu film at relatively low temperature and thus coherently inducing the ordering of FePt film led to the formation of the ordered FePt phase at a much lowered temperature. (c) 2005 American Institute of Physics.

引用

页数：3