The Effect of Pulse Plasma Treatment on the Corrosion Resistance of AISI 4140 Steel

被引:0
|
作者
Agdas, Gencer [1 ]
Demirkiran, A. Sukran [1 ]
Ozbek, Yildiz Yarali [1 ]
机构
[1] Sakarya Univ, Fac Engn, Dept Met & Mat Engn, TR-54187 Sakarya, Turkey
来源
INTERNATIONAL MULTIDISCIPLINARY MICROSCOPY CONGRESS | 2014年 / 154卷
关键词
SURFACE MODIFICATION; LAYER;
D O I
10.1007/978-3-319-04639-6_3
中图分类号
TH742 [显微镜];
学科分类号
摘要
Pulse plasma treatment is a surface modification treatment process, which is widely used to improve wear, fatigue and corrosion resistance of the industrial parts. The paper presents the results obtained from an experimental work investigating the changes in corrosion and microstructural surface properties of AISI 4140 steel. For the pulse plasma treatment, a battery capacity of 800 mu F, and three different sample plasma gun nozzle distances were used. The samples were subjected to micro-hardness measurements and it was found that the hardness values of modified surfaces are four times higher than untreated samples. The modified surface layers were examined using an optical microscope and X-ray analyses were carried out all samples. The new phases were found on surface. The samples were exposed to corrosion test in 0.5MNaCl aqueous solution. The corrosion behavior of samples was determined. An attempt was made to establish an empirical relationship between corrosion resistance and parameters of pulse plasma. The presence of modified layer has improved to corrosion resistance, and it was observed that corrosion cracks were initiated dominantly under the modified layer by pit formation mechanism.
引用
收藏
页码:19 / 25
页数:7
相关论文
共 50 条
  • [21] Effect of Magnetic Field Coupled Deep Cryogenic Treatment on Wear Resistance of AISI 4140 Steel
    Tang, Liang
    Yan, Xianguo
    Jiang, Yijiang
    Li, Fan
    Zhang, Haidong
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2020, 2020
  • [22] EXPERIMENTAL EVALUATION OF CORROSION RESISTANCE OF AN AISI - SAE 4140 STEEL IMPLANTED WITH NITROGEN IONS
    Pena, Dario
    Fontalvo, Paola
    Estupinan, Hugo
    Nino, Dannier
    Vesga, Wilson
    DYNA-COLOMBIA, 2009, 76 (159): : 43 - 52
  • [23] THE EFFECT OF NITROGEN ON THE CORROSION OF PLASMA-NITRIDED 4140 STEEL
    CHYOU, SD
    SHIH, HC
    CORROSION, 1991, 47 (01) : 31 - 34
  • [24] The Corrosion Enhancement due to Plasma Post-Oxidation Subsequent to Plasma Nitriding of a Steel AISI 4140
    Munoz-Castro, A. E.
    de la Piedad-Beneitez, A.
    Valencia-Alvarado, R.
    Lopez-Callejas, R.
    Mercado-Cabrera, A.
    Pena-Eguiluz, R.
    Rodriguez-Mendez, B. G.
    ACTA PHYSICA POLONICA A, 2015, 128 (05) : 824 - 827
  • [25] Surface Modification of AISI 4140 Steel Using Electrolytic Plasma Thermocyclic Treatment
    Kumruoglu, L. Cenk
    Ozel, Ahmet
    MATERIALS AND MANUFACTURING PROCESSES, 2010, 25 (09) : 923 - 931
  • [26] Sliding Wear Resistance of Borided AISI 4140 Steel
    Marquez-Cortes, R.
    Martinez-Trinidad, J.
    Flores-Martinez, M.
    Flores-Jimenez, M.
    Garcia-Leon, R. A.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (20) : 9101 - 9113
  • [27] Plasma post oxidation of nitrocarburized AISI 4140 steel
    Lee, Insup
    RARE METALS, 2006, 25 (6 SUPPL. 2) : 267 - 271
  • [28] Plasma post oxidation of nitrocarburized AISI 4140 steel
    LEE Insup
    RareMetals, 2006, (S2) : 267 - 271
  • [29] Effect of Pre-Oxidation on Plasma Nitrided Steel AISI4140
    Tang, Lei
    Zhao, Xiaobing
    Li, Jingcai
    Wei, Kunxia
    Hu, Jing
    METAL SCIENCE AND HEAT TREATMENT, 2020, 62 (3-4) : 224 - 228
  • [30] Sliding Wear Resistance of Borided AISI 4140 Steel
    R. Márquez-Cortés
    J. Martínez-Trinidad
    M. Flores-Martínez
    M. Flores-Jiménez
    R. A. García-León
    Journal of Materials Engineering and Performance, 2023, 32 : 9101 - 9113