Influence of the Heating Temperature and Fineness on the Hydration and Mechanical Property of Recycled Gypsum Plaster

被引：5

作者：

Li, Zhixin ^{[1
]}

Xu, Kaidong ^{[1
]}

Peng, Jiahui ^{[2
]}

Wang, Jina ^{[1
]}

Zhang, Jianwu ^{[1
]}

Li, Qingxiao ^{[1
]}

机构：

[1] Henan Univ Urban Construct, Sch Mat & Chem Engn, Pingdingshan 467036, Peoples R China

[2] Chongqing Univ, Coll Mat Sci & Engn, Chongqing 400045, Peoples R China

来源：

ADVANCES IN MATERIALS SCIENCE AND ENGINEERING | 2021年 / 2021卷

关键词：

CEMENT;

D O I：

10.1155/2021/7520378

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Influence of the heating temperature and fineness on the hydration and mechanical property of recycled gypsum plaster was investigated to find the suitable heating temperature and fineness. According to the results, the setting time of recycled gypsum plaster increased with the increase of heating temperature, and the mechanical strength increased first and then decreased at a temperature of 165 degrees C. Therefore, the suitable heating temperature was 165 degrees C, and at this time, the initial setting time and final setting time were 8 min and 12.5 min, respectively, which met the requirements of the Chinese standard of GB/T 9776-2008. The strength of recycled gypsum plaster increased with the increase of specific surface area, and the low water to plaster ratio and high strength were achieved when the specific surface area was 1526 m(2)/kg. Therefore, it can be concluded that the suitable heating temperature was 165 degrees C and the suitable specific surface area was 1526 m(2)/kg considering the properties and economics of recycled gypsum plaster.