Preparation of LaSrCoFeO3-x membranes

被引：78

作者：

Luyten, J ^{[1
]}

Buekenhoudt, A ^{[1
]}

Adriansens, W ^{[1
]}

Cooymans, J ^{[1
]}

Weyten, H ^{[1
]}

Servaes, F ^{[1
]}

Leysen, R ^{[1
]}

机构：

[1] Vlaamse Instelling Technol Onderzoek, B-2400 Mol, Belgium

来源：

SOLID STATE IONICS | 2000年 / 135卷 / 1-4期

关键词：

mixed conductor; ceramic membranes; synthesis;

D O I：

10.1016/S0167-2738(00)00425-2

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The last 10 years an alternative production route for oxygen production by using mixed conductors has been investigated. Perovskite mixed electron-oxygen conducting membranes are bulk membranes with a thickness of the order of 1 mm, showing sufficient oxygen fluxes only at temperatures above 800 degreesC. To reach commercially interesting fluxes at lower temperatures, membrane modules with a much higher surface/volume ratio or multilayer membranes with a thin dense skin need to be developed. In our laboratory, dense hollow fibres and porous multilayer substrates were synthesised. The hollow fibres were produced using a polymeric spinning technique based on phase inversion. The multilayer porous substrates were manufactured following conventional ceramic processing routes. (C) 2000 Elsevier Science B.V. All rights reserved.

引用

页码：637 / 642

页数：6