Effect of Low-Temperature Rolling on the Structure of Copper

被引：13

作者：

Kon'kova, T. N. ^{[1
]}

Mironov, S. Yu ^{[1
,2
]}

Danilenko, V. N. ^{[1
]}

Korznikov, A. V. ^{[1
]}

机构：

[1] Russian Acad Sci, Inst Met Superplast Problems, Ufa 450001, Russia

[2] Tohoku Univ, Dept Mat Proc, Grad Sch Engn, Sendai, Miyagi 9808579, Japan

来源：

PHYSICS OF METALS AND METALLOGRAPHY | 2010年 / 110卷 / 04期

关键词：

cryogenic deformation; rolling; copper; microstructure; texture; MG-SI ALLOY; PLASTIC-DEFORMATION; MECHANICAL-PROPERTIES; RECRYSTALLIZATION; MICROSTRUCTURE; ALUMINUM; PECULIARITIES; EXTRUSION; TEXTURES;

D O I：

10.1134/S0031918X10100029

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The influence of rolling at a liquid-nitrogen temperature on the microstructure of commercially pure copper has been investigated by the methods of transmission electron microscopy (TEM) and automated analysis of electron backscatter diffraction (EBSD) patterns. It has been established that the process of the structure formation was sufficiently complex and included a geometric effect of deformation, recrystallization, twinning, and fragmentation. It is shown that upon deformation to 50% the structure evolution was controlled by the Taylor-Polanyi principle. However, it was established that at larger reductions the formation of grain structure was determined by the competition between the geometric effect of deformation and recrystallization. The contribution of twinning and fragmentation to the structure formation was insignificant in the entire interval of deformations investigated. The recrystallization, apparently, was caused by the warming up of the sample to room temperature after low-temperature rolling.

引用

页码：318 / 330

页数：13

共 34 条

[1]

[Anonymous], 1997, Strength of Alloys. Part II. Deformation

[2] CRYSTALLOGRAPHIC TEXTURE, ANISOTROPIC YIELD SURFACES AND FORMING LIMITS OF SHEET METALS [J].

BARLAT, F .

MATERIALS SCIENCE AND ENGINEERING, 1987, 91 :55-72

[3] Submicrocristalline structure in copper after different severe plastic deformation schemes [J].

Dobatkin, S. V. ;

Salishchev, G. A. ;

Kuznetsov, A. A. ;

Kon'kova, T. N. .

RECRYSTALLIZATION AND GRAIN GROWTH III, PTS 1 AND 2, 2007, 558-559 :189-+

[4] Effect of microstructure on plastic deformation of Cu at low homologous temperatures [J].

Estrin, Y. ;

Isaev, N. V. ;

Lubenets, S. V. ;

Malykhin, S. V. ;

Pugachov, A. T. ;

Pustovalov, V. V. ;

Reshetnyak, E. N. ;

Fomenko, V. S. ;

Fomenko, L. S. ;

Shumilin, S. E. ;

Janecek, M. ;

Hellmig, R. J. .

ACTA MATERIALIA, 2006, 54 (20) :5581-5590

[5]

Gindin I. A., 1969, Fizika Metallov i Metallovedenie, V28, P466

[6]

Gindin I. A., 1967, FIZ MET METALLOVED, V23, P138

[7]

Gindin I. A., 1967, Fiz. Met. Metalloved, V24, P347

[8]

GINDIN IA, 1975, FIZ MET METALLOVED+, V39, P88

[9]

GINDIN IA, 1979, FIZ MET METALLOVED+, V48, P1004

[10]

GINDIN IA, 1966, DOKL AKAD NAUK SSSR+, V171, P552

← 1 2 3 4 →