Damage behavior of Nb3Sn/Cu superconducting strand at room temperature under asymmetric strain cycling

被引：4

作者：

Jiang, Lang ^{[1
,2
]}

Su, Xiyang ^{[1
,2
]}

Shen, Liuyang ^{[1
,2
]}

Zhou, Jun ^{[1
,2
]}

Zhang, Xingyi ^{[1
,2
]}

机构：

[1] Lanzhou Univ, Minist Educ China, Key Lab Mech Disaster & Environm Western China, Lanzhou 730000, Gansu, Peoples R China

[2] Lanzhou Univ, Coll Civil Engn & Mech, Dept Mech & Engn Sci, Lanzhou 730000, Gansu, Peoples R China

来源：

FUSION ENGINEERING AND DESIGN | 2021年 / 172卷 / 172期

关键词：

Asymmetric strain cycling; Damage evolution; Accumulated plastic strain; Stiffness degradation; Fatigue life; AXIS FATIGUE BEHAVIOR; FIBER-REINFORCED COMPOSITES; STIFFNESS DEGRADATION; MODEL; LIFE; PERFORMANCE; REDUCTION; MECHANICS; EVOLUTION; GEOMETRY;

D O I：

10.1016/j.fusengdes.2021.112869

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

In this study, damage evolution of Nb3Sn/Cu superconducting strand was investigated under asymmetric strain cycling. The results of the fatigue tests indicate that higher strain ranges and peaks can accelerate damage evolution, and damage evolution occurs seriously at the early fatigue stage. Based on the stiffness degradation rule of composites, two independent plastic damage evolution equations of the Nb3Sn sub-elements and Cu matrix were derived to obtain stiffness degradation and fatigue life by considering the effect of strain range and strain peak, respectively, and the accumulated plastic strain of Nb3Sn/Cu superconducting strands was obtained by deriving the total damage evolution equation. The proposed model was verified and validated by studying the fatigue behavior of Nb3Sn/Cu superconducting strands under asymmetric strain cycling. A good agreement between the analytical model and experimental data irrespective of the strain range and strain peak shows that the analytical model can not only predict the stiffness degeneration and accumulated plastic strain, but also describe the fatigue life of Nb3Sn/Cu superconducting strands under asymmetric strain cycling.

引用

页数：9

共 64 条

[51] Study of Filament Cracking Under Uniaxial Repeated Loading for ITER TF Strands [J].

Sheth, M. K. ;

Lee, P. J. ;

McRae, D. M. ;

Sanabria, C. M. ;

Starch, W. L. ;

Walsh, R. P. ;

Jewell, M. C. ;

Devred, A. ;

Larbalestier, D. C. .

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2012, 22 (03)

[52]

Shi WJ, 2011, ACTA MECH SOLIDA SIN, V24, P399

[53] Progress in the ITER Physics Basis - Chapter 1: Overview and summary [J].

Shimada, M. ;

Campbell, D. J. ;

Mukhovatov, V. ;

Fujiwara, M. ;

Kirneva, N. ;

Lackner, K. ;

Nagami, M. ;

Pustovitov, V. D. ;

Uckan, N. ;

Wesley, J. ;

Asakura, N. ;

Costley, A. E. ;

Donne, A. J. H. ;

Doyle, E. J. ;

Fasoli, A. ;

Gormezano, C. ;

Gribov, Y. ;

Gruber, O. ;

Hender, T. C. ;

Houlberg, W. ;

Ide, S. ;

Kamada, Y. ;

Leonard, A. ;

Lipschultz, B. ;

Loarte, A. ;

Miyamoto, K. ;

Mukhovatov, V. ;

Osborne, T. H. ;

Polevoi, A. ;

Sipps, A. C. C. .

NUCLEAR FUSION, 2007, 47 (06) :S1-S17

[54]

Sidoroff F., 1987, 6 INT C COMP MAT ECC

[55] The ITER remote maintenance system [J].

Tesini, A. ;

Palmer, J. .

FUSION ENGINEERING AND DESIGN, 2008, 83 (7-9) :810-816

[56] On the mechanical behavior of a Nb3Sn superconducting coil during a quench: Two-dimensional finite element analysis of a quench heater protected magnet [J].

Troitino, J. Ferradas ;

Ambrosio, G. ;

Bajas, H. ;

Brouwer, L. ;

Ferracin, P. ;

Bermudez, S. Izquierdo ;

Lorenzo Gomez, J. V. ;

Mangiarotti, F. J. ;

Perez, J. C. ;

Ravaioli, E. ;

Taakala, E. Tapani ;

Vallone, G. ;

Senatore, C. .

CRYOGENICS, 2020, 106

[57] FREQUENCY-EFFECTS ON THE FATIGUE LIFE AND DAMAGE OF GRAPHITE EPOXY COMPOSITES [J].

TSAI, GC ;

DOYLE, JF ;

SUN, CT .

JOURNAL OF COMPOSITE MATERIALS, 1987, 21 (01) :2-13

[58] Progressing in cable-in-conduit for fusion magnets: from ITER to low cost, high performance DEMO [J].

Uglietti, D. ;

Sedlak, K. ;

Wesche, R. ;

Bruzzone, P. ;

Muzzi, L. ;

della Corte, A. .

SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2018, 31 (05)

[59] A fatigue damage model for (0/90) FRP composites based on stiffness degradation of 0° and 90° composite plies [J].

Varvani-Farahani, A. ;

Shirazi, A. .

JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2007, 26 (13) :1319-1336

[60] A damage assessment model for cadaveric cortical bone subjected to fatigue cycles [J].

Varvani-Farahani, A. ;

Najmi, H. .

INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (02) :420-427

← 1 2 3 4 5 6 7 →