Evaluation of experimental phosphate and sulfur-based primer bonding to metal casting alloys

The aim of this study was to evaluate the effect of three experimental primers prepared with synthesized phosphorous and sulfur monomers (HEMA-P, ETMA and the mixture of HEMA-P/ETMA) on bonding to nickel-chromium (NiCr), silver-palladium (AgPd) and silver-gold (AgAu) metal alloys. The specimens were treated with experimental primers: HEMA-P, ETMA, HEMA-P/ETMA and Alloy Primer (Kuraray Noritake Dental Inc., Okayama, Japan) was used as commercial reference. Resin cement cylinders were built-up after application of tested primers on different alloy surfaces. Samples were stored in distilled water at 37 degrees C for 24 h before being subjected to shear bond tests using a mechanical testing machine. Shear bond strength (SBS) was recorded in MPa. Failure modes were classified under magnification as adhesive and mixed failure. Data were submitted to a two-way ANOVA and Student-Newman-Keuls' test. The statistically highest shear bond strength was observed with commercial primer to the AgPd alloy while the lowest value was shown with commercially available primers and experimental HEMA-P/ETMA to the NiCr alloy (p < 0.05). There was a predominance of adhesive failure, with the exception of commercially available primer, for which mixed failures were predominant. It could be concluded that formulations of metal primers containing HEMA-P or ETMA primers should be considered for use in the bonding protocol of NiCr alloys. (C) 2015 Elsevier Ltd. All rights reserved.