Phase composition, microstructure, mechanical properties, and wear performance of nanostructured Al2O3 and Al2O3-Y2O3 coatings deposited by plasma spraying

被引：37
作者：
Aghajani, Hossein [1 ]
Valefi, Zia [1 ]
Zamani, Pejman [1 ]
机构：
[1] Malek Ashtar Univ Technol, Fac Mat & Mfg Technol, Tehran, Iran
来源：
APPLIED SURFACE SCIENCE | 2022年 / 585卷
关键词：
Bi-modal microstructure; Phase composition; Bonding strength; Wear test; Nanostructured coating; Plasma spray; MICRO-INDENTATION; TITANIA COATINGS; ALUMINA; BEHAVIOR; CR2O3-AL2O3; FEEDSTOCK; POWDERS; CR2O3; APS;
D O I：
10.1016/j.apsusc.2022.152754
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
In this study, conventional and nanostructured Al2O3 and Al2O3-Y2O3 coatings were produced by atmospheric plasma spraying. Phase composition, microstructure and chemical composition studies were performed on the coatings. Microhardness, crack propagation resistance and bonding strength of the coatings were evaluated. Wear testing was also carried out by a pin-on-disc machine at loads of 2, 10 and 20 N. The results showed that the coatings obtained from nano-agglomerated powders had a Bi-modal microstructure. The addition of Y2O3 resulted in stabilizing desired alpha-Al2O3 phase. Nanostructured coatings displayed more increase in I alpha/I gamma than conventional types. Composite coatings showed higher bonding strength than individual Al2O3 coatings, due to the better adhesion of the splats, chemical bonding of Y2O3 and Al2O3, and the better melting and wetting of Y2O3 in the composite coatings. Nanostructured alumina coating had about twice crack propagation resistance more than conventional type. Despite the lower crack propagation resistance, conventional coatings showed higher wear resistance than nanostructured coatings due to their higher adhesion strength and hardness and denser microstructure.
引用
收藏
页数：17
相关论文
共 48 条
[1]   Pelletisation by tumbling as an alternative method of agglomerating nanometric particles for use as feedstock in bi-modal structured flame-sprayed ceramic coatings [J].
Alberto Arias, Jhoman ;
Milena Hurtado, Francy ;
Vargas, Freddy ;
Estrada, Geraldine ;
Cadavid, Edwin ;
Rincon Ortiz, Mauricio ;
Constanza Palacio, Claudia ;
Vargas, Fabio .
CERAMICS INTERNATIONAL, 2019, 45 (16) :20936-20944
[2]   Instrumented spherical micro-indentation of plasma-sprayed coatings [J].
Alcalá, J ;
Gaudette, F ;
Suresh, S ;
Sampath, S .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 316 (1-2) :1-10
[3]   Wear resistance and adhesive failure of thermal spray ceramic coatings deposited onto graphite in response to ultrasonic nanocrystal surface modification technique [J].
Amanov, A. .
APPLIED SURFACE SCIENCE, 2019, 477 :184-197
[4]  
Anderson A.E, 1992, FRICTION LUBRICATION, V18
[5]  
[Anonymous], 2008, The Science and Engineering of Thermal Spray Coatings
[6]   Influence of microstructure on the wear and corrosion behavior of detonation sprayed Cr2O3-Al2O3 and plasma sprayed Cr2O3 coatings [J].
Babu, P. Suresh ;
Sen, D. ;
Jyothirmayi, A. ;
Krishna, L. Rama ;
Rao, D. Srinivasa .
CERAMICS INTERNATIONAL, 2018, 44 (02) :2351-2357
[7]  
Basha GMT, 2020, MATER TODAY-PROC, V22, P1554
[8]   Microstructure and properties of Al2O3-ZrO2 composite coatings prepared by air plasma spraying [J].
Chen, Yi-da ;
Yang, Yong ;
Chu, Zhen-hua ;
Chen, Xue-guang ;
Wang, Lei ;
Liu, Zhe ;
Dong, Yan-chun ;
Yan, Dian-ran ;
Zhang, Jian-xin ;
Kang, Zhi-long .
APPLIED SURFACE SCIENCE, 2018, 431 :93-100
[9]   THE TRANSITION FROM MILD TO SEVERE WEAR IN ALUMINA DURING SLIDING [J].
CHO, SJ ;
MOON, H ;
HOCKEY, BJ ;
HSU, SM .
ACTA METALLURGICA ET MATERIALIA, 1992, 40 (01) :185-192
[10]   Fabrication and properties of plasma-sprayed Al2O3/TiO2 composite coatings: A role of nano-sized TiO2 addition [J].
Dejang, N. ;
Watcharapasorn, A. ;
Wirojupatump, S. ;
Niranatlumpong, P. ;
Jiansirisomboon, S. .
SURFACE & COATINGS TECHNOLOGY, 2010, 204 (9-10) :1651-1657
12345