Preparation of Si2N2O Ceramics by Spark Plasma Sintering

被引：3

作者：

Alekseeva, L. S. ^{[1
]}

Andreev, P., V ^{[1
]}

Drozhilkin, P. D. ^{[1
]}

Boldin, M. S. ^{[1
]}

Smetanina, K. E. ^{[1
]}

Murashov, A. A. ^{[1
]}

Karazanov, K. O. ^{[1
]}

Shcherbak, G., V ^{[1
]}

机构：

[1] Lobachevsky State Univ, Nizhnii Novgorod 603022, Russia

来源：

INORGANIC MATERIALS | 2022年 / 58卷 / 07期

关键词：

silicon oxynitride; spark plasma sintering; ceramics; density; SILICON-NITRIDE; MECHANICAL-PROPERTIES; MICROSTRUCTURE; FABRICATION; OXYNITRIDE;

D O I：

10.1134/S0020168522070020

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Powder mixtures based on Si3N4 nanoparticles and yttrium and aluminum oxides were prepared. Ceramic samples with a relative density of 95-96% have been produced by spark plasma sintering at a pressure of 80 MPa and a heating rate of 50 degrees C/min. The microstructure of the samples has been shown to be formed by Si2N2O grains similar to 0.7 mu m in size, with an amorphous oxide phase in between. The highest hardness (13.3 GPa) was reached by the sample containing the Y2O3 and Al2O3 oxides in the molar ratio 2 : 1 and obtained at a sintering temperature of 1770 degrees C.

引用

页码：772 / 777

页数：6

共 17 条

[1]

Andreev P. V., 2021, IOP Conference Series: Materials Science and Engineering, V1014, DOI 10.1088/1757-899X/1014/1/012002

[2]

Billy M., 1981, Ceramics International, V7, P13, DOI 10.1016/0272-8842(81)90033-X

[3] Comparative Study of Hot Pressing and High-Speed Electropulse Plasma Sintering of Al2O3/ZrO2/Ti(C,N) Powders [J].

Chuvil'deev, V. N. ;

Boldin, M. S. ;

Dyatlova, Ya. G. ;

Rumyantsev, V. I. ;

Ordanyan, S. S. .

RUSSIAN JOURNAL OF INORGANIC CHEMISTRY, 2015, 60 (08) :987-993

[4] Activated reaction synthesis of silicon oxynitride from silica and silicon nitride [J].

Fruhstorfer, Jens ;

Kerber, Florian ;

Weigelt, Christian ;

Moritz, Kirsten ;

Aneziris, Christos G. .

CERAMICS INTERNATIONAL, 2018, 44 (07) :8467-8475

[5] SEPARATION OF PARTICLE SIZE AND LATTICE STRAIN IN INTEGRAL BREADTH MEASUREMENTS [J].

HALDER, NC ;

WAGNER, CNJ .

ACTA CRYSTALLOGRAPHICA, 1966, 20 :312-&

[6] Fracture energy of an aligned porous silicon nitride [J].

Inagaki, Y ;

Ohji, T ;

Kanzaki, S ;

Shigegaki, Y .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (07) :1807-1809

[7]

Kawai C, 1997, J AM CERAM SOC, V80, P2705, DOI 10.1111/j.1151-2916.1997.tb03179.x

[8] Fabrication of silicon nitride nanoceramics - Powder preparation and sintering: A review [J].

Nishimura, Toshiyuki ;

Xu, Xin ;

Kimoto, Koji ;

Hirosaki, Naoto ;

Tanaka, Hidehiko .

SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2007, 8 (7-8) :635-643

[9] PROCESSING, MECHANICAL-PROPERTIES, AND OXIDATION BEHAVIOR OF SILICON OXYNITRIDE CERAMICS [J].

OHASHI, M ;

KANZAKI, S ;

TABATA, H .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1991, 74 (01) :109-114

[10]

Petzow G, 2002, STRUCT BOND, V102, P47

← 1 2 →