Effect of Y on microstructure, damping properties and mechanical properties of Cu-Al-Ni-Mn alloy

被引：13

作者：

Yang, Liu ^{[1
,2
]}

Jiang, Xiaosong ^{[1
,2
]}

Sun, Hongliang ^{[1
,2
]}

Shao, Zhenyi ^{[1
,2
]}

Fang, Yongjian ^{[3
]}

Shu, Rui ^{[4
]}

机构：

[1] Minist Educ, Key Lab Adv Technol Mat, Chengdu 610031, Peoples R China

[2] Southwest Jiaotong Univ, Sch Mat Sci & Engn, Chengdu 610031, Sichuan, Peoples R China

[3] Sungkyunkwan Univ, Sch Mech Engn, 2066 Seobu Ro, Suwon 16419, Gyeonggi Do, South Korea

[4] Forschungszentrum Julich, Inst Energieund Klimaforsch Plasmaphys IEK 4, D-52425 Julich, Germany

来源：

MATERIALS LETTERS | 2022年 / 308卷

基金：

中国博士后科学基金;

关键词：

Metals and alloys; Microstructure; Mechanical properties; Damping properties;

D O I：

10.1016/j.matlet.2021.131170

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of Y content on the microstructure, mechanical and damping properties of Cu-11Al-3Ni-2.5Mn-chi Y (chi = 0, 0.5, 1, 2, wt.%) alloys were investigated. The results of X-ray diffraction (XRD) analysis showed that the alloy was mainly composed of 18R martensite, alpha-Cu and gamma(2)-Cu9Al4. The Y2O3 particles appear after the addition of Y elements. The grain size is reduced to 36.5 mu m when 1 wt.% Y element was added, and the combined effect of the grain size reduction and the Y2O3 particles increases the tensile strength to 601.75 MPa. Meanwhile, the alloy at this content has high damping properties, the damping peaks at room temperature and temperature 600 degrees C were 0.038 and 0.24, respectively.

引用

页数：4

共 50 条

[31] Effect of Sc and Nd on the Microstructure and Mechanical Properties of Al-Mg-Mn Alloy [J].

Huizhong Li ;

Haijun Wang ;

Xiaopeng Liang ;

Yan Wang ;

Hongting Liu .

Journal of Materials Engineering and Performance, 2012, 21 :83-88

[32] Effect of Y on microstructure and mechanical properties of Al-Mg-Mn-Zr-Sc alloy with low Sc content [J].

Barkov, R. Yu. ;

Pozdniakov, A. V. ;

Tkachuk, E. ;

Zolotorevskiy, V. S. .

MATERIALS LETTERS, 2018, 217 :135-138

[33] Effect of thermomechanical treatment on the microstructure, phase composition, and mechanical properties of Al-Cu-Mn-Mg-Zr alloy [J].

Zuiko, I. S. ;

Gazizov, M. R. ;

Kaibyshev, R. O. .

PHYSICS OF METALS AND METALLOGRAPHY, 2016, 117 (09) :906-919

[34] Effect of Ce addition on microstructure, mechanical properties and corrosion behavior of Al-Cu-Mn-Mg-Fe alloy [J].

Tian, Wei ;

Hu, Mengnan ;

Chen, Xiaohong ;

Zhou, Honglei ;

Sun, Yue ;

Lu, Qingqing ;

Wan, Maoyuan .

MATERIALS RESEARCH EXPRESS, 2020, 7 (03)

[35] Effects of Y and Zn on mechanical properties and damping capacity of Mg-Cu-Mn alloy [J].

Wang Jing-feng ;

Wei Wen-wen ;

Li Long ;

Liang Hao ;

Pan Fu-sheng .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2010, 20 (10) :1846-1850

[36] Microstructure and mechanical properties of Al-Mg-Mn alloy with erbium [J].

Wang Xudong ;

Lin Shuangping ;

Yang Junjun ;

Tang Zhenlei ;

Nie Zuoren .

RARE METALS, 2012, 31 (03) :237-243

[37] Microstructure and mechanical properties of Al-Mg-Mn alloy with erbium [J].

WANG Xudong a LIN Shuangping b YANG Junjun b TANG Zhenlei c and NIE Zuoren d a School of Mechanical Engineering Taiyuan University of Technology Taiyuan China b Metal Working Engineering Department China Iron Steel Research Insititute Group Beijing China c Nonferous Metals Processing Division General Research Institute of Nonferrous Metal Beijing China d College of Materials Science and Engineering Beijing University of Technology Beijing China .

RareMetals, 2012, 31 (03) :237-243

[38] Microstructure and mechanical properties of Al-Mg-Mn alloy with erbium [J].

Xudong Wang ;

Shuangping Lin ;

Junjun Yang ;

Zhenlei Tang ;

Zuoren Nie .

Rare Metals, 2012, 31 :237-243

[39] Effect of Ce Content on the Microstructure and Mechanical Properties of Al-Cu-Li Alloy [J].

Ding, Xianxian ;

Lu, Yalin ;

Wang, Jian ;

Li, Xingcheng ;

Zhou, Dongshuai .

METALS, 2023, 13 (02)

[40] Effect of Chromium on Microstructure and Mechanical Properties of Al-Cu-Er-Zr Alloy [J].

Amer, S. M. ;

Glavatskikh, M. V. ;

Barkov, R. Yu. ;

Loginova, I. S. ;

Pozdnyakov, A. V. .

METALLURGIST, 2024, 67 (9-10) :1448-1456

← 1 2 3 4 5 →