Direct electrodeposition of highly dense 50 nm Bi2Te3-ySey nanowire arrays

被引:144
作者
Martín-González, M
Snyder, GJ
Prieto, AL
Gronsky, R
Sands, T
Stacy, AM
机构
[1] Univ Calif Berkeley, Dept Chem, Berkeley, CA 94720 USA
[2] CALTECH, Jet Prop Lab, Thermoelect Mat & Devices Team, Pasadena, CA 91109 USA
[3] Univ Calif Berkeley, Dept Mat Sci & Engn, Berkeley, CA 94720 USA
关键词
D O I
10.1021/nl034079s
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
Films and arrays of 200 and 50 nm diameter wires of Bi2Te3-xSex have been electrodeposited in the following general reaction: 2Bi(3+) + (3-y)HTeO2+ + (y)H2SeO3 + (9+y)H+ + 18e(-) --> Bi2Te3-ySey + (6+y)H2O. Films produced from an electrolyte of 0.0075 M Bi, 0,0090 M Te, and 0.0010 M Se in 1 M HNO3 at a potential of similar to0 V vs Ag/AgCl are single phase with composition Bi2Te2.6Se0.4 as determined by X-ray diffraction, energy-dispersive X-ray spectroscopy, and scanning electron microscopy. Similar conditions yield arrays of 200 and 50 nm Bi2Te3-ySey wires when deposited into porous alumina templates. The wires are single phase, crystalline, and textured, with up to 85% pore filling.
引用
收藏
页码:973 / 977
页数:5
相关论文
共 28 条
[1]   Significant decrease of the lattice thermal conductivity due to phonon confinement in a free-standing semiconductor quantum well [J].
Balandin, A ;
Wang, KL .
PHYSICAL REVIEW B, 1998, 58 (03) :1544-1549
[2]   Effect of phonon confinement on the thermoelectric figure of merit of quantum wells [J].
Balandin, A ;
Wang, KL .
JOURNAL OF APPLIED PHYSICS, 1998, 84 (11) :6149-6153
[3]   THERMOELECTRIC FIGURE OF MERIT OF QUANTUM-WIRE SUPERLATTICES [J].
BROIDO, DA ;
REINECKE, TL .
APPLIED PHYSICS LETTERS, 1995, 67 (01) :100-102
[4]   Transport properties of Bi1-xSbx alloy thin films grown on CdTe(111)B [J].
Cho, S ;
DiVenere, A ;
Wong, GK ;
Ketterson, JB ;
Meyer, JR .
PHYSICAL REVIEW B, 1999, 59 (16) :10691-10696
[5]  
*CRC, 1995, CRC HDB THERM
[6]  
Dresselhaus MS, 1999, MICROSCALE THERM ENG, V3, P89
[7]  
DRESSELHAUS MS, 1997, LOW DIMEMSIONAL THER, V16, P12
[8]   Development of thick-film thermoelectric microcoolers using electrochemical deposition [J].
Fleurial, JP ;
Borshchevsky, A ;
Ryan, MA ;
Phillips, WM ;
Snyder, JG ;
Caillat, T ;
Kolawa, A ;
Herman, JA ;
Mueller, P ;
Nicolet, M .
THERMOELECTRIC MATERIALS 1998 - THE NEXT GENERATION MATERIALS FOR SMALL-SCALE REFRIGERATION AND POWER GENERATION APPLICATIONS, 1999, 545 :493-500
[9]   Thermoelectric quantum-dot superlattices with high ZT [J].
Harman, TC ;
Taylor, PJ ;
Spears, DL ;
Walsh, MP .
JOURNAL OF ELECTRONIC MATERIALS, 2000, 29 (01) :L1-L4
[10]   EFFECT OF QUANTUM-WELL STRUCTURES ON THE THERMOELECTRIC FIGURE OF MERIT [J].
HICKS, LD ;
DRESSELHAUS, MS .
PHYSICAL REVIEW B, 1993, 47 (19) :12727-12731