Magnetic Properties of BaAlFe11O19 Hexaferrite with Different Morphologies

被引：5
作者：
Singhal, Sonal [1 ]
Namgyal, Tsering [1 ]
Singh, Jagdish [2 ]
Chandra, Kailash
Bansal, S. [3 ]
机构：
[1] Punjab Univ, Dept Chem, Chandigarh 160014, India
[2] Indian Inst Technol, Inst Instrumentat Ctr, Roorkee, Uttar Pradesh, India
[3] Indian Inst Technol, Dept Met & Mat Engn, Roorkee, Uttar Pradesh, India
来源：
MATERIALS AND MANUFACTURING PROCESSES | 2012年 / 27卷 / 01期
关键词：
Coercivity; Hexaferrite; Magnetization; Microscopy; Morphology; STRONTIUM FERRITE; PARTICLES; BARIUM;
D O I：
10.1080/10426914.2011.551961
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Sol-gel method is used to prepare BaAlFe11O19 hexaferrites, and the morphology of the samples has been changed by mixing the as obtained samples with inorganic template agents (KCl, KBr, and KI) during the annealing process. Fourier transform infrared spectroscopy (FTIR) frequency bands in the range 564-588 cm(-1) and 425-442 cm(-1) are corresponding to the formation of tetrahedral and octahedral clusters of metal oxides respectively. X-ray powder studies do not show any peak for the as obtained sample, however, regular X-ray diffraction (XRD) peaks were obtained for the samples annealed at 1000 degrees C. Magnetic measurement shows that the saturation magnetization (Ms) of BaAlFe11O19/KI is maximum (24.32 emu/g) and of BaAlFe11O19/KCl is minimum (9.47 emu/g). The coercivity (Hc) values of the sample with KCl is maximum (3237 Oe) and of the sample with KI is minimum (700 Oe).
引用
收藏
页码：65 / 68
页数：4
相关论文
共 19 条
  • [1] Effect of La3+ substitution on the structural, electrical and electrochemical properties of strontium ferrite by citrate combustion method
    Augustin, CO
    Selvan, RK
    Nagaraj, R
    Berchmans, LJ
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2005, 89 (2-3) : 406 - 411
  • [2] Barium ferrite thick films for microwave applications
    Capraro, S.
    Chatelon, J. P.
    Le Berre, M.
    Joisten, H.
    Rouiller, T.
    Bayard, B.
    Barbier, D.
    Rousseau, J. J.
    [J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2004, 272 : E1805 - E1806
  • [3] Carr R.L., 1965, Chem. Eng, V72, P163, DOI DOI 10.1016/J.JAEROSCI.2007.10.003
  • [4] Study on the synthesis of silver nanowires with adjustable diameters through the polyol process
    Chen, Chang
    Wang, Li
    Jiang, Guohua
    Zhou, Junfeng
    Chen, Xu
    Yu, Haojie
    Yang, Qiang
    [J]. NANOTECHNOLOGY, 2006, 17 (15) : 3933 - 3938
  • [5] Drofenik M., 2006, MATER MANUF PROCESS, V23, P603
  • [6] Magnetic properties of Sr-ferrites synthesized in molten (NaCl + KCl) flux
    Kim, Si-Dong
    Kim, Jung-Sik
    [J]. JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2006, 307 (02) : 295 - 300
  • [7] Klug H.P., 1974, XRAY DIFFRACTION PRO, V2nd, P992
  • [8] Li G.H., 2001, J SYNTH CRYSTALS, V16, P338
  • [9] MAY D, 2008, MATER MANUF PROCESS, V19, P777
  • [10] FTIR study of Ni, Cu and Zn substituted nano-particles of MgFe2O4
    Pradeep, A
    Chandrasekaran, G
    [J]. MATERIALS LETTERS, 2006, 60 (03) : 371 - 374
12