Effect of Particle Size Distribution of Calcined Diatomites on the Extinction Performance

被引：23

作者：

Du, Y. C. ^{[1
]}

Shi, S. L. ^{[1
]}

Bu, C. Y. ^{[1
]}

Dai, H. X. ^{[2
]}

Guo, Z. G. ^{[3
]}

Tang, G. Y. ^{[4
]}

机构：

[1] Beijing Univ Technol, Coll Mat Sci & Engn, Minist Educ, Key Lab Adv Funct Mat, Beijing 100124, Peoples R China

[2] Beijing Univ Technol, Coll Environm & Energy Engn, Lab Catalysis Chem & Nanosci, Dept Chem & Chem Engn, Beijing 100124, Peoples R China

[3] Beijing Dadi Yuantong Grp Co Ltd, Beijing, Peoples R China

[4] Langfang Nippon Co Ltd, Langfang, Hebei Province, Peoples R China

来源：

PARTICULATE SCIENCE AND TECHNOLOGY | 2011年 / 29卷 / 04期

关键词：

calcined diatomite; extinction; gloss; particle size distribution; sedimentation method;

D O I：

10.1080/02726351.2010.503263

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

Calcined diatomite was first investigated as matting agent for formulating high-performance coating. Jet milling and sieving or sedimentation methods were employed to obtain rational particle size distributions. It was found that the optimal size distribution of the particles with the diameters of D10=2.54 mu m, D25=5.04 mu m, D50=9.74 mu m, D75=18.80 mu m, and D90=31.66 mu m showed the best extinction performance, with the gloss and extinction being 2.9 and 3.3 and 32.6% and 50.7% determined at incidence angles of 60 degrees and 85 degrees, respectively.

引用

页码：368 / 377

页数：10

共 11 条

[1] Surface analysis of matt powder coatings [J].

Gunde, Marta Klanjsek ;

Kunaver, Matjaz ;

Cekada, Miha .

DYES AND PIGMENTS, 2007, 74 (01) :202-207

[2] Characterization and performances of an Algerian diatomite-based gas chromatography support [J].

Hadjadj-Aoul, O ;

Belabbes, R ;

Belkadi, M ;

Guermouche, MH .

APPLIED SURFACE SCIENCE, 2005, 240 (1-4) :131-139

[3]

JONES H, 1999, MODERN PAINT COATING, V1, P35

[4]

LIU TH, 1994, PAINT COATINGS IND, V1, P17

[5]

LIU YF, 2007, PRINCIPLE APPL COATI

[6]

MA LQ, 2001, COATINGS IND HDB

[7] Preparation of filter aids based on diatomites [J].

Martinovic, Sanja ;

Vlahovic, Milica ;

Boljanac, Tamara ;

Pavlovic, Ljubica .

INTERNATIONAL JOURNAL OF MINERAL PROCESSING, 2006, 80 (2-4) :255-260

[8] Photodegradation of water-based acrylic coatings containing silica [J].

Morrow, AM ;

Allen, NS ;

Edge, M .

JOURNAL OF COATINGS TECHNOLOGY, 1998, 70 (880) :65-72

[9]

SCHNEIDER H, 1994, JOCCA-SURF COAT INT, V77, P376

[10]

Wang D.Z., 1991, J INORGANIC MAT, V3, P354

← 1 2 →