Surface dynamics for poly(vinyl alkylate)s via dynamic contact angle and adhesion tension relaxation

被引:23
作者
Kasemura, T
Takahashi, S
Nakane, N
Maegawa, T
机构
[1] Department of Applied Chemistry, Faculty of Engineering, Gifu University, Gifu-shi 501-11
关键词
dynamic contact angle; adhesion tension relaxation; poly(vinyl alkylate);
D O I
10.1016/0032-3861(96)00177-2
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
Dynamic contact angle (DCA) and adhesion tension relaxation (ATR) for poly(vinyl alkylate)s (PVAls) were measured. Advancing contact angle initially increased with an increase in the side-chain-length and after a maximum at C10, it decreased, while receding contact angle showed a complex behaviour. A large contact-angle hysteresis was observed. DCA also depended on the dipping velocity. Results on ATRs showed that the surface molecule of these PVAls had large molecular mobility. Reproducibility of ATR was also observed. These phenomena were explained by the reorientation of the segment at polymer/water or polymer/air interface so as to minimize interfacial free energy. Copyright (C) 1996 Published by Elsevier Science Ltd.
引用
收藏
页码:3659 / 3664
页数:6
相关论文
共 14 条
[1]  
CHEN WY, 1986, J COLLOID INTERF SCI, V110, P486
[2]  
Damme H. S. V., 1986, J COLLOID INTERF SCI, V114, P167
[3]  
HOGT AH, 1985, J COLLOID INTERF SCI, V106, P289, DOI 10.1016/S0021-9797(85)80002-3
[4]   STUDIES ON THE ADSORPTION BEHAVIOR OF POLYMERS BY INTERFACIAL-TENSION .1. SURFACE AND INTERFACIAL-TENSIONS OF SOME POLY(ACRYLIC ESTER)S AND THEIR ACRYLIC-ACID COPOLYMERS [J].
KASEMURA, T ;
INAGAKI, M ;
HATA, T .
KOBUNSHI RONBUNSHU, 1987, 44 (02) :131-138
[5]   STUDIES ON SURFACE-TENSION OF POLYMERS IN RELATION TO THEIR STRUCTURE .7. SURFACE-TENSION OF POLY(ALKYLENE ISOPHTHALATE)S [J].
KASEMURA, T ;
KONDO, T ;
HATA, T .
KOBUNSHI RONBUNSHU, 1979, 36 (12) :815-820
[7]  
KASEMURA T, 1979, KOBUNSHI RONBUNSHU, V36, P337, DOI 10.1295/koron.36.337
[8]   SURFACE-TENSION OF ALKANEDIOLS AND THEIR CONDENSATION POLYMERS [POLY(ALKYLENE GLYCOL)S] - STUDIES ON SURFACE-TENSION OF POLYMERS IN RELATION TO THEIR STRUCTURES .3. [J].
KASEMURA, T ;
YAMASHITA, N ;
SUZUKI, K ;
KONDO, T ;
HATA, T .
KOBUNSHI RONBUNSHU, 1978, 35 (04) :215-222
[9]   STUDIES ON THE ADSORPTION BEHAVIOR OF POLYMERS BY INTERFACIAL-TENSION .3. INTERFACIAL-TENSION OF POLY(PROPYLENE GLYCOL)S AND THEIR BLOCK COPOLYMERS WITH POLY(ETHYLENE GLYCOL)S AGAINST POLYETHYLENE AND POLYVINYL ACETATE) [J].
KASEMURA, T ;
YAMAGUCHI, S ;
HATTORI, K ;
HATA, T .
KOBUNSHI RONBUNSHU, 1988, 45 (01) :63-68
[10]   STUDIES ON THE ADSORPTION BEHAVIOR OF POLYMERS BY INTERFACIAL-TENSION .2. MOLECULAR-WEIGHT DEPENDENCE OF INTERFACIAL-TENSION OF POLY(ETHYLENE GLYCOL)S [J].
KASEMURA, T ;
YAMAGUCHI, S ;
HATA, T .
KOBUNSHI RONBUNSHU, 1987, 44 (09) :657-662