Wear behavior of thermally sprayed coatings under different loading conditions

被引：10
作者：
Duan, DL [1 ]
Li, S
Duan, XH
Li, SZ
机构：
[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China
[2] Liming Aeroengine Grp Corp, Shenyang 110043, Peoples R China
来源：
TRIBOLOGY TRANSACTIONS | 2005年 / 48卷 / 01期
基金：
中国国家自然科学基金;
关键词：
wear-resistant coating; wear mechanisms; testing; material properties;
D O I：
10.1080/05698190590896915
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Wear behavior of three kinds of thermally sprayed coatings with similar hardness have been investigated under steady-state and dynamic loading tests. The steady-state loading tests were conducted on a reciprocating sliding device and the dynamic loading tests were conducted with a single-pendulum scratching device. Experimental results show that the wear mechanisms of the coatings under steady-state sliding friction testing are microcutting and microploughing, whereas the material losses under the dynamic impact scratch testing are mainly due to split cutting and fracture. Tribo-oxidization in the sliding process was found to have an influence on the wear behaviors of the thermally sprayed coatings. The results also indicated that wear resistance of thermally sprayed coatings can be correlated to hardness, plasticity, toughness, and cohesion. As far as the coatings of similar hardness were concerned, the wear resistance under steady-state loading was mainly due to the cohesion of the laminar structure of the coatings and the wear resistance under dynamic loading was mainly clue to the toughness and deformation compatibility of the coatings.
引用
收藏
页码：45 / 50
页数：6
相关论文
共 10 条
[1]  
Bryggmar U., 1979, P 2 INT C WEAR MAT D, P292
[2]  
DAI ZD, 2000, TRIBOLOGY, V20, P175
[3]   Determination of dynamic mechanical properties of metals from single pendulum scratch tests [J].
Hu, WY ;
Li, S ;
Li, SZ ;
Sun, XF ;
Guan, HR .
TRIBOLOGY INTERNATIONAL, 1999, 32 (03) :153-160
[4]   EVALUATION OF ABRADABILITY OF POROUS SEAL MATERIALS IN A SINGLE-PENDULUM SCRATCH DEVICE [J].
LIANG, YN ;
LI, SZ ;
LI, S .
WEAR, 1994, 177 (02) :167-173
[5]   Some developments for single-pass pendulum scratching [J].
Liang, YN ;
Li, SZ ;
Li, DF ;
Li, S .
WEAR, 1996, 199 (01) :66-73
[6]  
LIU HW, 1997, J SW JIAOTONG U, V32, P341
[7]   Tribological behaviour of plasma-sprayed WC coatings with and without laser remelting [J].
Mateos, J ;
Cuetos, JM ;
Fernández, E ;
Vijande, R .
WEAR, 2000, 239 (02) :274-281
[8]   Design aspects for advanced tribological surface coatings [J].
Matthews, A ;
Leyland, A ;
Holmberg, K ;
Ronkainen, H .
SURFACE & COATINGS TECHNOLOGY, 1998, 100 (1-3) :1-6
[9]   THE ROLE OF OXIDATION IN THE FRICTION AND WEAR BEHAVIOR OF SOLID-SOLUTION CU-AL ALLOYS IN RECIPROCATING SLIDING CONTACT WITH SAPPHIRE AND D2 TOOL STEEL [J].
POGGIE, RA ;
WERT, JJ .
WEAR, 1992, 156 (02) :315-326
[10]  
Ren J.R., 2000, TRIBOLOGY, V20, P18
1