Impermeability of Y3Al5O12 ceramic against molten glassy calcium-magnesium-alumina-silicate

被引：15
作者：
Xue, Zhaolu
Ma, Yue
Gong, Shengkai
Guo, Hongbo [1 ]
机构：
[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100083, Peoples R China
来源：
CHINESE JOURNAL OF AERONAUTICS | 2018年 / 31卷 / 12期
基金：
中国国家自然科学基金;
关键词：
Calcium-magnesium-alumina-silicate (CMAS); Ceramics; Thermal barrier coating; Yttrium aluminum garnet; Zirconia; THERMAL BARRIER COATINGS; HIGH-TEMPERATURE ATTACK; PHASE-STABILITY; CONDUCTIVITY; RESISTANCE;
D O I：
10.1016/j.cja.2018.02.007
中图分类号：
V [航空、航天];
学科分类号：
08 ; 0825 ;
摘要：
Degradation of thermal barrier coatings (TBCs) caused by calcium-magnesium-aluminasilica (CMAS) glassy penetration is becoming an urgent issue for TBCs industrial applications. In this work, yttrium aluminum garnet (Y3Al5O12, YAG) nano-powders were synthesized through a chemical co-precipitation route. The resistance of YAG ceramic to glassy CMAS infiltration at 1250 degrees C was evaluated. YAG ceramic bulk sintered at 1700 degrees C for 10 h was comprised of a single garnet-type Y3Al5O12 phase. The molten CMAS glass was suppressed on the surface of the YAG ceramic at 1250 degrees C. A chemical reaction between YAG and the molten CMAS glass did not occur at 1250 degrees C for 24 h, suggesting that YAG could act as an impermeable material against glassy CMAS deposits in the TBC field. (C) 2018 Chinese Society of Aeronautics and Astronautics. Production and hosting by Elsevier Ltd.
引用
收藏
页码：2306 / 2311
页数：6
相关论文
共 26 条
  • [1] Novel thermal barrier coatings that are resistant to high-temperature attack by glassy deposits
    Aygun, Aysegul
    Vasiliev, Alexander L.
    Padture, Nitin P.
    Ma, Xinqing
    [J]. ACTA MATERIALIA, 2007, 55 (20) : 6734 - 6745
  • [2] Microstructure characteristics of EB-PVD YSZ thermal barrier coatings corroded by molten volcanic ash
    Cai, Canying
    Chang, Sheng
    Zhou, Yichun
    Yang, Li
    Zhou, Guangwen
    Wang, Yanguo
    [J]. SURFACE & COATINGS TECHNOLOGY, 2016, 286 : 49 - 56
  • [3] Ceramic materials for thermal barrier coatings
    Cao, XQ
    Vassen, R
    Stoever, D
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (01) : 1 - 10
  • [4] Calcium-magnesium-alumina-silicate (CMAS) delamination mechanisms in EB-PVD thermal barrier coatings
    Chen, X
    [J]. SURFACE & COATINGS TECHNOLOGY, 2006, 200 (11) : 3418 - 3427
  • [5] Materials design for the next generation thermal barrier coatings
    Clarke, DR
    Levi, CG
    [J]. ANNUAL REVIEW OF MATERIALS RESEARCH, 2003, 33 : 383 - 417
  • [6] Thermal barrier coatings technology: critical review, progress update, remaining challenges and prospects
    Darolia, R.
    [J]. INTERNATIONAL MATERIALS REVIEWS, 2013, 58 (06) : 315 - 348
  • [7] Composition effects of thermal barrier coating ceramics on their interaction with molten Ca-Mg-Al-silicate (CMAS) glass
    Drexler, Julie M.
    Ortiz, Angel L.
    Padture, Nitin P.
    [J]. ACTA MATERIALIA, 2012, 60 (15) : 5437 - 5447
  • [8] Air-plasma-sprayed thermal barrier coatings that are resistant to high-temperature attack by glassy deposits
    Drexler, Julie M.
    Shinoda, Kentaro
    Ortiz, Angel L.
    Li, Dongsheng
    Vasiliev, Alexander L.
    Gledhill, Andrew D.
    Sampath, Sanjay
    Padture, Nitin P.
    [J]. ACTA MATERIALIA, 2010, 58 (20) : 6835 - 6844
  • [9] Plasma-sprayed La2Ce2O7 thermal barrier coatings against calcium-magnesium-alumina-silicate penetration
    Gao, Lihua
    Guo, Hongbo
    Gong, Shengkai
    Xu, Huibin
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2014, 34 (10) : 2553 - 2561
  • [10] Phase stability of plasma sprayed YAG-YSZ composite beads/coatings at high temperature
    Gu, Lijian
    Zhao, Sumei
    Xu, Haying
    Hui, Yu
    Fan, Xizhi
    Zou, Binglin
    Wang, Ying
    Cao, Xueqiang
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2013, 33 (15-16) : 3325 - 3333
123