Microstructure Evolution and High-Temperature Compressibility of Modified Two-Step Strain-Induced Melt Activation-Processed Al-Mg-Si Aluminum Alloy

被引:4
作者
Lin, Chia-Wei [1 ]
Hung, Fei-Yi [1 ]
Lui, Truan-Sheng [1 ]
Chen, Li-Hui [1 ]
机构
[1] Natl Cheng Kung Univ, Dept Mat Sci & Engn, Tainan 701, Taiwan
关键词
aluminum alloy; strain-induced melting activation (SIMA); semi-solid metal processing; high-temperature compression; MECHANICAL-PROPERTIES; BEHAVIOR; SYSTEM;
D O I
10.3390/met6050113
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A two-step strain-induced melt activation (TS-SIMA) process that omits the cold working step of the traditional strain-induced melt activation (SIMA) process is proposed for 6066 Al-Mg-Si alloy to obtain fine, globular, and uniform grains with a short-duration salt bath. The results show that increasing the salt bath temperature and duration leads to a high liquid phase fraction and a high degree of spheroidization. However, an excessive salt bath temperature leads to rapid grain growth and generates melting voids. The initial degree of dynamic recrystallization, which depends on the extrusion ratio, affects the globular grain size. With an increasing extrusion ratio, the dynamic recrystallization becomes more severe and the dynamic recrystallized grain size becomes smaller. It results in the globular grains becomes smaller. The major growth mechanism of globular grains is Ostwald ripening. Furthermore, high-temperature compressibility can be improved by the TS-SIMA process. After a 4 min salt bath at 620 degrees C, the high-temperature compression ratio become higher than that of a fully annealed alloy. The results show that the proposed TS-SIMA process has great potential.
引用
收藏
页数:13
相关论文
共 23 条
[1]   CHARACTERIZATION OF GLOBULAR MICROSTRUCTURE IN NMS PROCESSED ALUMINUM A356 ALLOY: THE ROLE OF CASTING SIZE [J].
Akhlaghi, F. ;
Farhood, A. H. S. .
ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES II, PTS 1 AND 2, 2011, 264-265 :1868-1877
[2]  
ASM International Alloy Phase Diagram and the Handbook Committees, 1992, ASM HDB, V3, P307
[3]   Coarsening of equiaxed microstructure in the semisolid state of aluminum 7075 alloy through SIMA processing [J].
Bolouri, Amir ;
Shahmiri, Mohammad ;
Kang, Chung Gil .
JOURNAL OF MATERIALS SCIENCE, 2012, 47 (08) :3544-3553
[4]   The effect of strain-induced melt activation process on the microstructure and mechanical properties of Ti-refined A6070 Al alloy [J].
Emamy, M. ;
Razaghian, A. ;
Karshenas, M. .
MATERIALS & DESIGN, 2013, 46 :824-831
[5]   Semisolid metal processing [J].
Fan, Z .
INTERNATIONAL MATERIALS REVIEWS, 2002, 47 (02) :49-85
[6]   OSTWALD RIPENING IN A SYSTEM WITH A HIGH VOLUME FRACTION OF COARSENING PHASE [J].
HARDY, SC ;
VOORHEES, PW .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (11) :2713-2721
[7]  
Hatch J.E., 1984, ALUMINUM PROPERTIES, V1, P50
[8]   Development of process design system for press forming-multi-objective optimization of intermediate die shape in transfer forming [J].
Katayama, T ;
Nakamachi, E ;
Nakamura, Y ;
Ohata, T ;
Morishita, Y ;
Murase, H .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 155 :1564-1570
[9]  
Laughlm D.E., 1998, MINER MET MAT SOC, P63
[10]   Crystallization, high temperature deformation behavior and solid-to-solid formability of a Ti-based bulk metallic glass within supercooled liquid region [J].
Lee, Kwang Seok ;
Kim, Seongwook ;
Lim, Ka Ram ;
Hong, Sung Hwan ;
Kim, Ki Buem ;
Na, Young Sang .
JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 663 :270-278