Effects of additives on the mechanical and thermal properties of epoxy-based nanocomposites produced using sonication

Epoxy nanocomposites were synthesized in the presence of hydroxyapatite with the aid of an ultrasonicator. In general, as the amount of hydroxyapatite increased from 0wt% to 10wt%, the mechanical properties of the hydroxyapatite-containing nanocomposite were enhanced. The mechanical properties of the nanocomposite were significantly enhanced by the simple addition of 10 wt% of hydroxyapatite. Specifically, the storage modulus of the 10 wt% hydroxyapatite-containing nanocompsote was 3.2GPa, which is 46% higher compared to that of the pristine epoxy nanocomposite. The glass transition temperature of hydroxyapatite-containing nanocomposites generally decreased by few degrees in Celsius. To investigate the effect of additives on the mechanical properties of the epoxy-based nanocomposite, nanocomposites were synthesized using both montmorillonite and tellurium dioxide instead of hydroxyapatite. Intrestingly, both additive-based nanocomposite materials resulted in an increase in the storage modulus while the glass transition temperature decreased. These results demonstrate that the addition of few wt% of all three additives (hydroxyapatite, montmorillonite, and tellurium dioxide) can enhance the mechanical properties of epoxy-based nanocomposites.