Superficial defects induced by argon and oxygen bombardments on (110) Ti02 surfaces

Compositional and chemical changes of titanium dioxide monocrystalline surfaces induced by bombardment with 4 keV argon and oxygen ions have been studied by AES, XPS and AFM. Argon ion bombardment induced strong changes in the composition and chemical stale of the surface: loss of oxygen due to preferential sputtering occurred, and, related to this, Ti4+ species were reduced to Ti3+ and Ti2+. During oxygen bombardment, competition between preferential sputtering of oxygen ions of the oxide surface and oxygen implantation was observed. This phenomenon was found to be strongly dependent upon the incidence angle of the oxygen ions. Moreover, an oxygen bombardment with normal incidence of the surface that had been previously submitted to an argon ion bombardment led to a restoichiometrization of the surface: no further Ti3+ or Ti2+ was found by XPS, only Ti4+, (C) 1998 Elsevier Science B.V. All rights reserved.