Static and dynamic corrosion fatigue of Mg alloys used in automotive industry

被引：14

作者：

Eliezer, A

Haddad, J

Unigovski, Y

Gutman, EM

机构：

[1] Negev Acad Coll Engn, Dept Civil Engn, IL-84100 Beer Sheva, Israel

[2] Ben Gurion Univ Negev, Dept Mat Engn, IL-84105 Beer Sheva, Israel

来源：

MATERIALS AND MANUFACTURING PROCESSES | 2005年 / 20卷 / 01期

关键词：

magnesium alloys; corrosion fatigue; corrosion creep; 3.5 %NaCl- and borate buffer; solutions; emulsion of NaCl solution in gear oil; die casting; extrusion; fitting equations; relative fatigue life; size effect;

D O I：

10.1081/AMP-200041636

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Corrosion fatigue tests were carried out on die-cast and extruded magnesium alloys AZ91D, AZ80, AM50, and ZK60 in air, and NaCl-based and borate solutions. N-sot/N-air ratios (the relative fatigue life) were used for analysis of the corrosion fatigue behavior of Mg alloys in various environments, where N-sol and N-air are the numbers of cycles to failure in the solution and in air, respectively. Extruded ZK60 alloy reveals very high fatigue and corrosion fatigue properties in comparison with other alloys. However, it has the lowest relative fatigue life (N-sol/N-air similar to 10(-3) - 10(-2)) or the highest sensitivity to the action of NaCl-based solutions in comparison with that of AM50 and AZ31 alloys (N-sol/N-air similar to 10(-2) - 10(-1)). Under the same stress, the corrosion fatigue life of extruded alloys is significantly longer than that of die-cast alloys (N-sol for extruded AM50 in NaCl is two to three times longer than that of die-cast AM50). The synergistic effect of corrosion and stress on viscoelasticity of magnesium alloys called corrosion creep is shown. The highest sensitivity to creep in a corrosive environment is observed in the alloy with the highest Al content.

引用

页码：75 / 88

页数：14

共 13 条

[1]

Eliezer A, 1998, CORROS REV, V16, P1

[2]

Eliezer A., 2001, J. Light Metals, V1, P179, DOI [10.1016/S1471-5317(01)00011-6, DOI 10.1016/S1471-5317(01)00011-6]

[3]

Galun R, 1998, CORROS REV, V16, P53

[4]

Gutman E. M., 1994, Mechanochemistry of Solid Surfaces, P322

[5] Mechanoelectrochemical behavior and creep corrosion of magnesium alloys [J].

Gutman, EM ;

Eliezer, A ;

Unigovski, Y ;

Abramov, E .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 302 (01) :63-67

[6]

GUTMAN EM, 2000, LIGHT METAL AGE DEC, P16

[7]

GUTMAN EM, 2000, LIGHT METAL AGE DEC, P15

[8]

GUTMAN EM, 2000, LIGHT METAL AGE DEC, P14

[9]

HILPERT M, 2000, MAGNESIUM ALLOYS THE, P463

[10] MECHANISM OF STRESS-CORROSION CRACKING IN THE AZ31B MAGNESIUM ALLOY [J].

LOGAN, HL .

JOURNAL OF RESEARCH OF THE NATIONAL BUREAU OF STANDARDS, 1958, 61 (06) :503-508

← 1 2 →