Corrosion study of the graphene oxide and reduced graphene oxide-based epoxy coatings

被引:71
作者
Ghauri, Faizan Ali [1 ,2 ]
Raza, Mohsin Ali [1 ]
Baig, Muhammad Saad [1 ]
Ibrahim, Shoaib [1 ]
机构
[1] Univ Punjab, CEET, Dept Met & Mat Engn, Lahore 54590, Pakistan
[2] Univ Punjab, CEET, Dept Met & Mat Engn, Adv Mat Res Lab, Lahore 54590, Pakistan
关键词
coatings; reduced graphene oxide; graphene oxide; electrochemical impedance spectroscopy; WATER; PROTECTION; COPPER; FILMS;
D O I
10.1088/2053-1591/aa9aac
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This work aims to determine the effect of graphene oxide (GO) and reduced graphene oxide (rGO) incorporation as filler on the corrosion protection ability of epoxy coatings in saline media. GO was derived from graphite powder following modified Hummers' method, whereas rGO was obtained after reduction of GO with hydrazine solution. About 1 wt.% of GO or rGO were incorporated in epoxy resin by solution mixing process followed by ball milling. GO and rGO-based epoxy composite coatings were coated on mild steel substrates using film coater. The coated samples were characterized by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization tests after 1 and 24 h immersion in 3.5% NaCl. The results suggested that GO-based epoxy composite coatings showed high impedance and low corrosion rate.
引用
收藏
页数:9
相关论文
共 26 条
[1]  
Barsoukov E, 2005, IMPEDANCE SPECTROSCOPY: THEORY, EXPERIMENT, AND APPLICATIONS, 2ND EDITION, P1, DOI 10.1002/0471716243
[2]   Advanced anticorrosive coatings prepared from electroactive polyimide/graphene nanocomposites with synergistic effects of redox catalytic capability and gas barrier properties [J].
Chang, K. C. ;
Hsu, C. H. ;
Lu, H. I. ;
Ji, W. F. ;
Chang, C. H. ;
Li, W. Y. ;
Chuang, T. L. ;
Yeh, J. M. ;
Liu, W. R. ;
Tsai, M. H. .
EXPRESS POLYMER LETTERS, 2014, 8 (04) :243-255
[3]   Room-temperature cured hydrophobic epoxy/graphene composites as corrosion inhibitor for cold-rolled steel [J].
Chang, Kung-Chin ;
Hsu, Min-Hsiang ;
Lu, Hsin-I ;
Lai, Mei-Chun ;
Liu, Pei-Ju ;
Hsu, Chien-Hua ;
Ji, Wei-Fu ;
Chuang, Tsao-Li ;
Wei, Yen ;
Yeh, Jui-Ming ;
Liu, Wei-Ren .
CARBON, 2014, 66 :144-153
[4]   Inhibition and promotion of electrochemical reactions by graphene in organic coatings [J].
Chaudhry, A. U. ;
Mittal, Vikas ;
Mishra, Brajendra .
RSC ADVANCES, 2015, 5 (98) :80365-80368
[5]  
Deen K.M., 2009, J QUALITY TECHNOLOGY, V5, P6
[6]   The rise of graphene [J].
Geim, A. K. ;
Novoselov, K. S. .
NATURE MATERIALS, 2007, 6 (03) :183-191
[7]   Investigation on the temperature-dependent growth rate of carbon nanotubes using chemical vapor deposition of ferrocene and acetylene [J].
Kim, KE ;
Kim, KJ ;
Jung, WS ;
Bae, SY ;
Park, J ;
Choi, J ;
Choo, J .
CHEMICAL PHYSICS LETTERS, 2005, 401 (4-6) :459-464
[8]   Passivation of microbial corrosion using a graphene coating [J].
Krishnamurthy, A. ;
Gadhamshetty, V. ;
Mukherjee, R. ;
Chen, Z. ;
Ren, W. ;
Cheng, H-M. ;
Koratkar, N. .
CARBON, 2013, 56 :45-49
[9]   Self-aligned graphene as anticorrosive barrier in waterborne polyurethane composite coatings [J].
Li, Yaya ;
Yang, Zhenzhen ;
Qiu, Hanxun ;
Dai, Yigang ;
Zheng, Qingbin ;
Li, Jing ;
Yang, Junhe .
JOURNAL OF MATERIALS CHEMISTRY A, 2014, 2 (34) :14139-14145
[10]   Graphene dip coatings: An effective anticorrosion barrier on aluminum [J].
Liu, Jianhua ;
Hua, Lei ;
Li, Songmei ;
Yu, Mei .
APPLIED SURFACE SCIENCE, 2015, 327 :241-245