Gigacycle Fatigue Properties of Hydrogen-Charged JIS-SCM440 Low-Alloy Steel Under Ultrasonic Fatigue Testing

被引：22

作者：

Furuya, Yoshiyuki ^{[1
]}

Hirukawa, Hisashi ^{[1
]}

Hayakawa, Masao ^{[1
]}

机构：

[1] Natl Inst Mat Sci, Tsukuba, Ibaraki 3050047, Japan

来源：

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2010年 / 41A卷 / 09期

关键词：

S-N CURVE; CRACK-PROPAGATION; STRENGTH; FAILURE; BEHAVIOR; INITIATION; MECHANISM; GROWTH;

D O I：

10.1007/s11661-010-0307-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Gigacycle fatigue tests were conducted on hydrogen-charged low-alloy steel. In this study, high- and low-strength specimens were prepared to investigate the effects of hydrogen on internal and surface fractures, respectively. The fatigue tests were conducted mainly by ultrasonic fatigue testing at 20 kHz and additionally by conventional servohydraulic fatigue testing at 50 Hz. All high-strength specimens revealed internal fractures. The fatigue strength of the hydrogen-charged specimens was much lower than that of the uncharged specimens. In the low-strength specimens, the uncharged specimens revealed surface fractures in the short-life regions in addition to internal fractures in the long-life regions. However, the hydrogen-charged specimens revealed internal fractures only that were combined with a much lower fatigue strength. The difference in fracture surfaces was small between the hydrogen-charged and the uncharged specimens, whereas the optically dark areas of the hydrogen-charged specimens seemed smaller than those of the uncharged specimens.

引用

页码：2248 / 2256

页数：9

共 35 条

[1] Gigacycle fatigue properties of 1800 MPa class spring steels [J].

Abe, T ;

Furuya, Y ;

Matsuoka, S .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2004, 27 (02) :159-167

[2]

Bathias C., 2004, Gigacycle fatigue in mechanical practice

[3] THERMAL-ANALYSIS OF TRAPPED HYDROGEN IN PURE IRON [J].

CHOO, WY ;

LEE, JY .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (01) :135-140

[4] Crack growth behaviour of heat-treated 4140 steel in air and gaseous hydrogen [J].

Chuang, JH ;

Tsay, LW ;

Chen, C .

INTERNATIONAL JOURNAL OF FATIGUE, 1998, 20 (07) :531-536

[5]

Emura H., 1989, T JPN SOC MECH ENG A, V55, P45

[6]

Frith PH., 1955, J IRON STEEL I, V180, P26

[7] Specimen size effects on gigacycle fatigue properties of high-strength steel under ultrasonic fatigue testing [J].

Furuya, Y. .

SCRIPTA MATERIALIA, 2008, 58 (11) :1014-1017

[8] 1010-cycle fatigue properties of 1800 MPa-class JIS-SUP7 spring steel [J].

Furuya, Y ;

Abe, T ;

Matsuoka, S .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2003, 26 (07) :641-645

[9] Gigacycle fatigue properties for high-strength low-alloy steel at 100 Hz, 600 Hz, and 20 kHz [J].

Furuya, Y ;

Matsuoka, S ;

Abe, T ;

Yamaguchi, K .

SCRIPTA MATERIALIA, 2002, 46 (02) :157-162

[10] Evaluation of giga-cycle fatigue properties of some maraging steels by intermittent ultrasonic fatigue testing [J].

Ishii, H ;

Yagasaki, T ;

Akagi, H .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2002, 25 (8-9) :831-835

← 1 2 3 4 →