Effect of aluminium content on the coating structure and dross formation in the hot-dip galvanizing process

被引:44
作者
Shawki, S [1 ]
Hamid, ZA [1 ]
机构
[1] Cent Met R&D Inst, Cairo, Egypt
关键词
galvanizing; aluminizing; hot dipping process; dross;
D O I
10.1002/sia.1608
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Hot dipping of steel in aluminium-zinc baths of varying composition (5-90% Al) has been undertaken with the aim of elucidating the mechanism of coating formation. On the basis of these experiments, it has been possible to define a range of aluminium content over which there is a change from a normal galvanizing process to a typical aluminizing process. Alternatively, the coating structure and properties were markedly affected by the aluminium content of the dipping bath. The kinetics of such coatings acquires the character of the activation energy Ea. The effect of various silicon levels as an inhibitor to iron dissolution during hot dipping at different aluminium percentages was studied. The structure of dross formation in 55 wt.% Al-Zn was identified. The adverse effect of heavy accumulation of dross in the dipping pot on the coating structure also was shown. Copyright (C) 2003 John Wiley Sons, Ltd.
引用
收藏
页码:943 / 947
页数:5
相关论文
共 11 条
[1]   REACTION MECHANISMS FOR COATINGS FORMED DURING HOT DIPPING OF IRON IN 0 TO 10 PCT AL-ZN BATHS AT 450 DEGREES TO 700 DEGREES C [J].
GHUMAN, ARP ;
GOLDSTEIN, JI .
METALLURGICAL TRANSACTIONS, 1971, 2 (10) :2903-+
[2]  
Hansen M., 1958, CONSTITUTION BINARY, DOI DOI 10.1149/1.2428700
[3]   ALUMINUM-RICH ALLOY LAYERS FORMED DURING HOT DIP GALVANIZING OF LOW-CARBON STEEL [J].
HARVEY, GJ ;
MERCER, PD .
METALLURGICAL TRANSACTIONS, 1973, 4 (02) :619-621
[4]  
JERC H, 1964, STRUCTURE PROPERTIES, V2
[5]  
JONES RD, 1980, P INT 80, P371
[6]  
KOSTER W, 1970, Z METALLKD, V61, P649
[7]  
PERROT P, 1988, P 15 INT GALV C ROM
[8]   THE EFFECTS OF SILICON ON THE REACTION BETWEEN SOLID IRON AND LIQUID 55 WT PCT AL-ZN BATHS [J].
SELVERIAN, JH ;
MARDER, AR ;
NOTIS, MR .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1989, 20 (03) :543-555
[9]  
SELVERIAN JH, 1988, METALL T A, V19, P1139
[10]  
SPITTLE JA, 1988, P 15 INT GALV C ROM