Molten salt synthesis of SrFeO3 nanocrystals

被引:10
作者
Yang, Jun [1 ]
Li, Runsheng [1 ,2 ]
Li, Xiaoci [1 ]
Long, Yulin [1 ]
Zhou, Junyi [1 ]
Zhang, Yuanming [1 ]
机构
[1] Jinan Univ, Dept Chem, Guangzhou 510632, Guangdong, Peoples R China
[2] Guangzhou 2 Middle Sch, Guangzhou 510530, Guangdong, Peoples R China
关键词
Perovskite oxides; Molten salt synthesis; X-ray diffraction; THIN-FILMS; PEROVSKITES; LA;
D O I
10.2109/jcersj2.119.736
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Pure perovskite compound SrFeO3 nanocrystals were successfully synthesized in molten NaNO3-KNO3 eutectic with Na2O2 from a mixture of strontium nitrate and ferric nitrate. The effect of metal precursors, salt medium, annealing temperature (mainly 400-800 degrees C), and oxidizing properties of the melt on the phase composition, crystallite size and morphology of the resulting metal oxides were systematically studied by simultaneous TG/DSC, X-ray diffraction (XRD), scanning electron microscopy (SEM) methods. The results showed that the formation of the SrFeO3 phase mainly depended on the nature of the metal precursor and salt medium. It was found that metal nitrates are the suitable precursors and NaNO3-KNO3 eutectic with Na2O2 is the suitable salt medium, which results in the formation of pure SrFeO3 nanocrystals at a much lower temperature of 400 degrees C. (C)2011 The Ceramic Society of Japan. All rights reserved.
引用
收藏
页码:736 / 739
页数:4
相关论文
共 25 条
[11]  
Majid A, 2007, MATER RES SOC SYMP P, V972, P391
[12]   Lanthanum-based perovskites obtained in molten nitrates or nitrites [J].
Matei, C. ;
Berger, D. ;
Marote, P. ;
Stoleriu, S. ;
Deloume, J. P. .
PROGRESS IN SOLID STATE CHEMISTRY, 2007, 35 (2-4) :203-209
[13]   Combustion synthesis of La0.2Sr0.8Cr0.2Fe0.8O3-x [J].
Ming, Q ;
Hung, J ;
Yang, YL ;
Nersesyan, M ;
Jacobson, AJ ;
Richardson, JT ;
Luss, D .
COMBUSTION SCIENCE AND TECHNOLOGY, 1998, 138 (1-6) :279-296
[14]   Flux syntheses of La-doped NaTaO3 and its photocatalytic activity [J].
Porob, Digamber G. ;
Maggard, Paul A. .
JOURNAL OF SOLID STATE CHEMISTRY, 2006, 179 (06) :1727-1732
[15]   PREPARATION OF STRONTIUM FERRITE PARTICLES BY SPRAY-PYROLYSIS [J].
SENZAKI, Y ;
CARUSO, J ;
HAMPDENSMITH, MJ ;
KODAS, TT ;
WANG, LM .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (11) :2973-2976
[16]   Low temperature synthesis and characterization of rare earth orthoferrites LnFeO3 (Ln = La, Pr and Nd) from molten NaOH flux [J].
Shivakumara, C. .
SOLID STATE COMMUNICATIONS, 2006, 139 (04) :165-169
[17]   Microstructure and high temperature transport properties of high quality epitaxial SrFeO3-δ films [J].
Solis, C. ;
Rossell, M. D. ;
Garcia, G. ;
Figueras, A. ;
Van Tendeloo, G. ;
Santiso, J. .
SOLID STATE IONICS, 2008, 179 (35-36) :1996-1999
[18]   A CO-TAP study of the reducibility of La1-xSrxFe(Pd)O3±δ perovskites [J].
Song, Zhaoxia ;
Nishiguchi, Hiroyasu ;
Liu, Wei .
APPLIED CATALYSIS A-GENERAL, 2006, 306 :175-183
[19]   Magnetization and magnetoresistance in insulating phases of SrFeO3-δ -: art. no. 054424 [J].
Srinath, S ;
Kumar, MM ;
Post, ML ;
Srikanth, H .
PHYSICAL REVIEW B, 2005, 72 (05)
[20]  
WANG DS, 2008, J APPL PHYS, V104