Moisture-assisted crack growth at epoxy-glass interfaces

被引：42

作者：

Ritter, JE ^{[1
]}

Fox, JR ^{[1
]}

Hutko, DI ^{[1
]}

Lardner, TJ ^{[1
]}

机构：

[1] Univ Massachusetts, Dept Mech & Ind Engn, Amherst, MA 01003 USA

来源：

JOURNAL OF MATERIALS SCIENCE | 1998年 / 33卷 / 18期

基金：

美国国家科学基金会;

关键词：

D O I：

10.1023/A:1004477006957

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The double cleavage drilled compression (DCDC) test was used to measure the critical energy release rate, moisture-assisted crack growth, and fatigue threshold for epoxy-glass interfaces bonded with and without a silane coupling agent. The DCDC specimen consists of two glass beams (either soda-lime or fused silica) bonded together with an epoxy adhesive. A through-the-thickness hole is drilled in the centre of the specimen. In the DCDC test compressive loading causes tensile stresses to develop at the poles of the drilled hole. Cracks then nucleate in the epoxy-glass interface, extend from the poles, and propagate axially along the interface in primarily mode I loading. The resistance to moisture-assisted crack growth at untreated epoxy-glass interfaces is significantly less than that in monolithic glass specimens. However, the resistance to moisture-assisted crack growth at silane bonded epoxy-glass interfaces can be comparable with or greater than that in monolithic glass. Silane bonding of epoxy to glass is more effective with fused silica than soda-lime glass, with the fatigue limit of silane bonded epoxy-fused silica interfaces being about 2.5 times greater than that for silane bonded epoxy-soda-lime glass. These results are discussed in terms of possible interfacial crack growth mechanisms. (C) 1998 Kluwer Academic Publishers.

引用

页码：4581 / 4588

页数：8

共 22 条

[1]

Doremus R.H., 1973, GLASS SCI

[2] CRACK DEFLECTION AT AN INTERFACE BETWEEN DISSIMILAR ELASTIC-MATERIALS [J].

HE, MY ;

HUTCHINSON, JW .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1989, 25 (09) :1053-1067

[3] ANALYSIS OF THE DOUBLE CLEAVAGE DRILLED COMPRESSION SPECIMEN FOR INTERFACE FRACTURE ENERGY MEASUREMENTS OVER A RANGE OF MODE MIXITIES [J].

HE, MY ;

TURNER, MR ;

EVANS, AG .

ACTA METALLURGICA ET MATERIALIA, 1995, 43 (09) :3453-3458

[4]

HELFINSTINE JD, 1992, PHYSICS OF NON-CRYSTALLINE SOLIDS, P654

[5]

ILER RK, 1975, CHEM SILICA

[6]

Janssen C., 1974, P 10 INT C GLASS, P23

[7]

Kinloch A. J., 1987, ADHES ADHES

[8]

KINLOCH AJ, 1996, P I MECH ENG LOND

[9] Toughening of impenetrable interfaces by monodisperse tethered polymer chains: Effect of areal attachment density [J].

Lin, R ;

Quirk, RP ;

Kuang, J ;

Penn, LS .

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 1996, 10 (04) :341-349

[10] Toughening of impenetrable interfaces by polydisperse tethered polymer chains: Effect of tethered chain length [J].

Lin, R ;

Wang, H ;

Kalika, DS ;

Penn, LS .

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 1996, 10 (04) :327-339

← 1 2 3 →