Effect of non-isothermal aging on microstructure and properties of Al-5.87Zn-2.07Mg-2.42Cu alloys

被引：16

作者：

Li, Yao ^{[1
,2
]}

Xu, Guo-fu ^{[1
,2
]}

Peng, Xiao-yan ^{[1
]}

Liu, Shi-chao ^{[1
]}

Deng, Ying ^{[1
]}

Liang, Xiao-peng ^{[1
]}

机构：

[1] Cent South Univ, Sch Mat Sci & Engn, Changsha 410083, Peoples R China

[2] Cent South Univ, Key Lab Nonferrous Met Mat Sci & Engn, Minist Educ, Changsha 410083, Peoples R China

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2021年 / 31卷 / 10期

基金：

中国国家自然科学基金;

关键词：

Al-Zn-Mg-Cu aluminum alloy; non-isothermal aging; eta ' phases; mechanical properties; MG-CU ALLOY; MECHANICAL-PROPERTIES; CORROSION BEHAVIOR; PRECIPITATION; STRENGTH; GROWTH;

D O I：

10.1016/S1003-6326(21)65701-1

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The evolution of microstructure and properties of Al-5.87Zn-2.07Mg-2.42Cu alloys during non-isothermal aging was studied. The mechanical properties of the alloy were tested by stretching at room temperature. The results show that in the non-isothermal aging process, when the alloy is cooled to 140 degrees C, the ultimate tensile strength of the alloy reaches a maximum value of 582 MPa and the elongation is 11.9%. The microstructure was tested through a transmission electron microscope, and the experimental results show that the GP zones and eta' phases are the main strengthening precipitates. At the cooling stage, when the temperature dropped to 180 degrees C, the GP zones were precipitated again. Besides, the experimental results show that the main strengthening phase during non-isothermal aging is eta' phases.

引用

页码：2899 / 2908

页数：10

共 22 条

[1] VOLUME FREE ENERGY CHANGE ASSOCIATED WITH PRECIPITATE NUCLEATION [J].

AARONSON, HI ;

KINSMAN, KR ;

RUSSELL, KC .

SCRIPTA METALLURGICA, 1970, 4 (02) :101-&

[2] Influence of roll speed difference on microstructure, texture and mechanical properties of 7075 aluminum plates produced via combined continuous casting and rolling process [J].

Amiri, Mohammad Mehdi ;

Fereshteh-Saniee, Faramarz .

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2021, 31 (04) :901-912

[3] Overview no. 130 - Size effects in materials due to microstructural and dimensional constraints: A comparative review [J].

Arzt, E .

ACTA MATERIALIA, 1998, 46 (16) :5611-5626

[4] GP-zones in Al-Zn-Mg alloys and their role in artificial aging [J].

Berg, LK ;

Gjonnes, J ;

Hansen, V ;

Li, XZ ;

Knutson-Wedel, M ;

Waterloo, G ;

Schryvers, D ;

Wallenberg, LR .

ACTA MATERIALIA, 2001, 49 (17) :3443-3451

[5] Additivity and isokinetic behaviour in relation to particle dissolution [J].

Bjorneklett, BI ;

Grong, O ;

Myhr, OR ;

Kluken, AO .

ACTA MATERIALIA, 1998, 46 (17) :6257-6266

[6] Recent developments in advanced aircraft aluminium alloys [J].

Dursun, Tolga ;

Soutis, Costas .

MATERIALS & DESIGN, 2014, 56 :862-871

[7] Characterization of precipitation and phase transformations in Al-Zn-Mg alloy by the differential dilatometry [J].

Hadjadj, L. ;

Amira, R. ;

Hamana, D. ;

Mosbah, A. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 462 (1-2) :279-283

[8] The effects of non-isothermal aging on the strength and corrosion behavior of Al-Zn-Mg-Cu alloy [J].

Jiang, Daming ;

Liu, Yuan ;

Liang, Shuai ;

Xie, Wenlong .

JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 681 :57-65

[9] Effect of friction welding conditions and aging treatment on mechanical properties of A7075-T6 aluminium alloy friction joints [J].

Kimura, M ;

Choji, M ;

Kusaka, M ;

Seo, K ;

Fuji, A .

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2005, 10 (04) :406-412

[10] Effect of ageing treatment on fatigue crack growth of die forged Al-5.87Zn-2.07Mg-2.42Cu alloy [J].

Li, Yao ;

Xe, Guofu ;

Liu, Shichao ;

Peng, Xiaoyan ;

Yin, Zhimin ;

Wang, Li ;

Liang, Xiaopeng .

ENGINEERING FRACTURE MECHANICS, 2019, 215 :251-260

← 1 2 3 →