Effect of repetitive corrugation and straightening on Al and Al-0.25Sc alloy

被引：50
作者：
Rajinikanth, V. [1 ]
Arora, Gaurav [2 ]
Narasaiah, N. [1 ]
Venkateswarlu, K. [1 ]
机构：
[1] Natl Met Lab, Div Mat Sci & Technol, Jamshedpur 831007, Bihar, India
[2] Punjab Engn Coll, Dept Met Engn, Chandigarh 160012, India
来源：
MATERIALS LETTERS | 2008年 / 62卷 / 02期
关键词：
aluminum; repetitive corrugation and straightening; deformation; hardness;
D O I：
10.1016/j.matlet.2007.05.014
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The improvement in strength of Al and Al-0.2Sc alloys through repetitive corrugation and straightening (RCS) was studied. The RCS was carried out using both single teeth as well as multiple teeth corrugative setup attached to a universal testing machine. The improvement in strength was obtained by measuring the hardness after processing. The rotation of sample by 90 degrees between successive passes resulted in higher hardness values as compared to the simple bending and straightening. The increment in hardness obtained with same number of passes in the case of Al-0.2Sc alloy is more as compared to Al and is possibly due to blocking of dislocations that are introduced during deformation by Al3SC precipitates. (c) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码：301 / 304
页数：4
相关论文
共 21 条
[1]   Overview no. 130 - Size effects in materials due to microstructural and dimensional constraints: A comparative review [J].
Arzt, E .
ACTA MATERIALIA, 1998, 46 (16) :5611-5626
[2]   CONSTITUTION AND AGE HARDENING OF AL-SC ALLOYS [J].
BLAKE, N ;
HOPKINS, MA .
JOURNAL OF MATERIALS SCIENCE, 1985, 20 (08) :2861-2867
[3]   THE EARLY STAGES OF SOLUTE DISTRIBUTION BELOW A TRANSITION-TEMPERATURE [J].
COHEN, JB .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (10) :2685-2697
[4]  
Furukawa M, 2001, ADV ENG MATER, V3, P121, DOI 10.1002/1527-2648(200103)3:3<121::AID-ADEM121>3.0.CO
[5]  
2-V
[6]   Development of repetitive corrugation and straightening [J].
Huang, JY ;
Zhu, YT ;
Alexander, DJ ;
Liao, XZ ;
Lowe, TC ;
Asaro, RJ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 371 (1-2) :35-39
[7]   Microstructures and dislocation configurations in nanostructured Cu processed by repetitive corrugation and straightening [J].
Huang, JY ;
Zhu, YT ;
Jiang, H ;
Lowe, TC .
ACTA MATERIALIA, 2001, 49 (09) :1497-1505
[8]  
INDAL PKV, 2006, MATER LETT, V60, P3373
[9]   Principle of equal-channel angular pressing for the processing of ultra-fine grained materials [J].
Iwahashi, Y ;
Wang, JT ;
Horita, Z ;
Nemoto, M ;
Langdon, TG .
SCRIPTA MATERIALIA, 1996, 35 (02) :143-146
[10]   Properties and deformation behaviour of severe plastic deformed aluminium alloys [J].
Leo, P. ;
Cerri, E. ;
De Marco, P. P. ;
Roven, H. J. .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 182 (1-3) :207-214
123