Fatigue crack propagation at sharp notches

被引：0

作者：

Wurm, B ^{[1
]}

Pham, VB ^{[1
]}

Sahn, S ^{[1
]}

机构：

[1] Tech Univ Dresden, Inst Festkorpermech, D-8027 Dresden, Germany

来源：

FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4 | 1999年

关键词：

D O I：

暂无

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Crack propagation from different sharp notches was observed especially in low cycle fatigue tests under 4-point-bending with constant amplitudes. Cracks were measured using the replication method. Two materials with different microstructures were examined. For description the stress intensity factor for cracks from notches by Smith/Miller [2] and the crack closure formula by Newman [3] were used. Nominal stresses greater than the yield stress were corrected with an elastic-plastic assumption. The crack closure of small cracks was included in an extension with d(0)* [4]. The description with the SIF gives good results when a plasticity correction is used.

引用

页码：1163 / 1168

页数：6

共 50 条

[21] STUDY OF FATIGUE CRACK INITIATION IN THE VICINITY OF NOTCHES [J].

SAANOUNI, K ;

BATHIAS, C .

ENGINEERING FRACTURE MECHANICS, 1982, 16 (05) :695-706

[22] Research on the direction of fatigue crack propagation resulting from sharp concentrators of stress [J].

Surovin, PG ;

Tikhomirov, VM .

INTERNATIONAL JOURNAL OF FRACTURE, 2004, 128 (1-4) :25-32

[23] Short fatigue crack propagation from notches in N18NI based superalloy [J].

Sansoz, F ;

Brethes, B ;

Pineau, A .

ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, :61-66

[24] FATIGUE CRACK-GROWTH AND COALESCENCE AT NOTCHES [J].

FRISE, PR ;

BELL, R .

INTERNATIONAL JOURNAL OF FATIGUE, 1992, 14 (01) :51-56

[25] Fatigue crack propagation [J].

Totten, George .

ADVANCED MATERIALS & PROCESSES, 2008, 166 (05) :39-41

[26] Fatigue crack propagation [J].

G.E. Totten and Associates LLC, 514 N. 86th Street, Seattle, WA 98103, United States .

Adv Mater Processes, 2008, 5 (39-41)

[27] Initiation and propagation of cracks at sharp notches under cyclic loading [J].

Wurm, B ;

Sähn, S ;

Pham, VB .

LOW CYCLE FATIGUE AND ELASTO-PLASTIC BEHAVIOUR OF MATERIALS, 1998, :553-558

[28] A modelling of zigzag-like cracks propagation at sharp notches [J].

Semenov, AS ;

Sähn, S ;

Pham, VB .

FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, :1199-1204

[29] Mode I fatigue crack growth at notches considering crack closure [J].

Savaidis, G. ;

Savaidis, A. ;

Zerres, P. ;

Vormwald, M. .

INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (10) :1543-1558

[30] Two methods for predicting the multiaxial fatigue limits of sharp notches [J].

Susmel, L ;

Taylor, D .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2003, 26 (09) :821-833

← 1 2 3 4 5 →