Synthesis and morphological characterization of nanocrystalline powders obtained by a gas condensation method

被引:20
作者
Djekoun, A
Bouzabata, B
Alleg, S
Greneche, JM
Otmani, A
机构
[1] Univ Annaba, Inst Phys, Unite Rech Mat Met, Annaba 23000, Algeria
[2] Univ Maine, Lab Phys Etat Condense, CNRS, UPRES A 6087, F-72085 Le Mans 9, France
来源
ANNALES DE CHIMIE-SCIENCE DES MATERIAUX | 1998年 / 23卷 / 04期
关键词
D O I
10.1016/S0151-9107(98)80111-6
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
The preparation of nanocrystalline powders of Fe and Fe50Ni50 has been performed by a gas-condensation method under pure helium atmosphere. The characterization of the prepared materials which was carried out by means of Transmission Electron Microscopy, X-rays diffraction and Mossbauer Spectrometry, evidences for the presence of oxide phases. Fe and FeNi based ultrafine particles are observed with a size comprised within the range 10-70 nm and they occur as clusters or chains.
引用
收藏
页码:557 / 562
页数:6
相关论文
共 23 条
[1]  
Birringer R., 1986, T JAPAN I METALS S, V27, P43
[2]   CHARACTERISTICS OF NANOPHASE TIAL PRODUCED BY INERT-GAS CONDENSATION [J].
CHANG, H ;
ALTSTETTER, CJ ;
AVERBACK, RS .
JOURNAL OF MATERIALS RESEARCH, 1992, 7 (11) :2962-2970
[3]  
CULITY BD, 1972, INTRO MAGNETIC MAT, P103
[4]  
EASTERLING KE, 1971, PHYS SINTERING, P79
[5]   STRUCTURAL AND THERMODYNAMIC PROPERTIES OF NANOCRYSTALLINE FCC METALS PREPARED BY MECHANICAL ATTRITION [J].
ECKERT, J ;
HOLZER, JC ;
KRILL, CE ;
JOHNSON, WL .
JOURNAL OF MATERIALS RESEARCH, 1992, 7 (07) :1751-1761
[6]  
Rofagha R., 1993, Nanostructured Materials, V2, P1, DOI [10.1016/0965-9773(93)90180-J, 10.1016/0965-9773(93)90044-C]
[7]   NANOCRYSTALLINE METALS PREPARED BY HIGH-ENERGY BALL MILLING [J].
FECHT, HJ ;
HELLSTERN, E ;
FU, Z ;
JOHNSON, WL .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (09) :2333-2337
[8]  
GLEITER H, 1984, Z METALLKD, V75, P263
[9]   NANOCRYSTALLINE MATERIALS [J].
BIRRINGER, R .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 117 :33-43
[10]   NANOCRYSTALLINE SOLIDS [J].
GLEITER, H .
JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1991, 24 :79-90