Non-Destructive Characterization of Subsurface Residual Stress Fields and Correlation with Microstructural Conditions in a Shot-Peened Inconel Component

被引:6
作者
Park, J. -S. [1 ]
Yildizli, K. [2 ]
Demir, E. [3 ]
Dawson, P. R. [4 ]
Miller, M. P. [4 ]
机构
[1] Argonne Natl Lab, Adv Photon Source, Lemont, IL 60439 USA
[2] Ondokuz Mayis Univ, Dept Mech Engn, Fac Engn, TR-55200 Atakum, Samsun, Turkey
[3] Sabanci Univ, Fac Engn & Nat Sci, TR-34956 Istanbul, Turkey
[4] Cornell Univ, Sibley Sch Mech & Aerosp Engn, Ithaca, NY 14853 USA
基金
美国国家科学基金会;
关键词
Shot-peening; Residual stress; X-ray diffraction; Finite element method; Nickel superalloy; X-RAY-DIFFRACTION; DEFORMATION HETEROGENEITY; PLASTIC-DEFORMATION; GRAIN-REFINEMENT; DISTRIBUTIONS; SURFACE; STRAIN; RELAXATION; EVOLUTION; REPRESENTATION;
D O I
10.1007/s11340-018-0418-z
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Shot-peening is an important surface treatment used in a preventative way to guard against fatigue failures. The residual stress state imparted by shot-peening deters the formation and propagation of surface cracks. In this paper, we describe the measurement of residual stresses in an Inconel, IN100, sample using lattice strains measured using High Energy X-ray Diffraction (HEXD) and a Bi-Scale Optimization Method (BSOM). HEXD enabled rapid, non-destructive lattice strain measurements over a large region of the sample. Subsurface strains were obtained using a conical slit setup. The BSOM utilizes a macroscale representation of the sample and a spherical harmonic-based crystal scale representation of crystal orientation space at each experimental point (diffraction volume). A roughly biaxial stress state was predicted with a von Mises equivalent stress between 300 MPa and 400 MPa near the surface. The layer of material with high residual stress induced by shot-peening was found to be approximately 1 mm thick. Diffraction peak width, EBSD, and microhardness measurements were also made on the same sample, which rendered more qualitative measures of the plasticity-related effects of the shot-peening induced residual stress field. All of these measurements show a dimishing shot-peening plasticity with the increasing depth.
引用
收藏
页码:1389 / 1406
页数:18
相关论文
共 58 条
[1]   ON THE SYMMETRIES OF SPHERICAL HARMONICS [J].
ALTMANN, SL ;
BRADLEY, CJ .
PHILOSOPHICAL TRANSACTIONS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1963, 255 (1054) :199-215
[2]  
[Anonymous], ED PSYCHOL
[3]  
[Anonymous], HKL TECHNOLOGY CHANN
[4]  
[Anonymous], NUCL INSTRUMENTS M A
[5]   CRYSTAL ROTATIONS REPRESENTED AS RODRIGUES VECTORS [J].
BECKER, R ;
PANCHANADEESWARAN, S .
TEXTURES AND MICROSTRUCTURES, 1989, 10 (03) :167-194
[6]   ELEMENT-FREE GALERKIN METHODS [J].
BELYTSCHKO, T ;
LU, YY ;
GU, L .
INTERNATIONAL JOURNAL FOR NUMERICAL METHODS IN ENGINEERING, 1994, 37 (02) :229-256
[7]   Relaxation of shot-peened residual stresses under creep loading [J].
Buchanan, Dennis J. ;
John, Reji .
SCRIPTA MATERIALIA, 2008, 59 (03) :286-289
[8]  
Bunge, 1982, TEXTURE ANAL MAT SCI
[9]   Assessment of surface hardening effects from shot peening on a Ni-based alloy using electron backscatter diffraction techniques [J].
Child, D. J. ;
West, G. D. ;
Thomson, R. C. .
ACTA MATERIALIA, 2011, 59 (12) :4825-4834
[10]   Correlation of diffraction peak broadening to crystal strengthening in finite element simulations [J].
Dawson, PR ;
Boyce, DE ;
Rogge, RB .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 399 (1-2) :13-25