Optical and electrical properties of Te-substituted Sn-Sb-Se semiconducting thin films

Thin films of Sn10Sb20Se70-XTeX (0 <= X <= 14) composition were deposited using thermal evaporation technique. As-prepared films were amorphous as studied by X-ray diffraction. Surface morphology studies revealed that films have surface roughness similar to 2 nm and av. grain size similar to 30 nm. Optical band gap E-g showed a sharp decrease for initial substitution of Se with Te upto 2 at.%. A broad hump in the optical band gap is observed for further substitution of Se with Te. The trend of optical band gap variation with tellurium content has been qualitatively explained using band model given by Kastner. The dc-conductivity measurements showed thermally activated conduction with single activation energy for the measured temperature regime and followed Meyer-Neldel rule. The dc-activation energy has nearly half the value as that of optical band gap that revealed the intrinsic nature of semiconductor. The annealing below glass transition T-g led to decrease in optical band gap as well as dc-activation energy that might be related to increase of disorder in material with annealing. (c) 2011 Elsevier B.V. All rights reserved.