Nanocrystalline MCrAlY bond coat for thermal barrier coating applications

被引：0

作者：

Ajdelsztajn, L ^{[1
]}

He, JH ^{[1
]}

Kim, GE ^{[1
]}

Provenzano, V ^{[1
]}

Lavernia, EJ ^{[1
]}

Schoenung, JM ^{[1
]}

机构：

[1] Univ Calif Davis, Dept Chem Engn & Mat Sci, Davis, CA 95616 USA

来源：

SURFACE ENGINEERING: IN MATERIALS SCIENCE II | 2003年

关键词：

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This work describes recent progress in improving the oxidation behavior of the bond coat using HVOF nanostructured MCrAlY coatings. NiCrAlY powder was cryomilled and HVOF sprayed onto a Ni-based alloy. Oxidation experiments were performed on the coating to form the thermally grown oxide layer (TGO). The formation of the oxide phases on top of the bond coat after heat treatment at 1000degreesC was analyzed (morphology and composition) for different heat treatment times. In the nanostructured coatings, the presence of a homogeneous alpha-Al2O3 layer was observed. The nanostructured characteristic of the coating and the presence of Al2O3 within the cryomilled powders enhance the nucleation of the TGO alumina layer which protects the coating from further oxidation and avoids the formation of mixed oxide protrusions presented on the coating sprayed using the as-received powder. The cryomilling process of the MCrAlY powders has shown to be effective in improving the oxidation behavior of the coatings used in turbine engines applications.

引用

页码：71 / 80

页数：10

共 50 条

[21] The al-enriched γ′-Ni3Al-base bond coat for thermal barrier coating applications [J].

Liu, Chen ;

Chen, Ying ;

Qiu, Lin ;

Liu, Han ;

Bai, Mingwen ;

Xiao, Ping .

CORROSION SCIENCE, 2020, 167

[22] Characterization and understanding of residual stresses in a NiCoCrAlY bond coat for thermal barrier coating application [J].

Chen, Y. ;

Zhao, X. ;

Dang, Y. ;

Xiao, P. ;

Curry, N. ;

Markocsan, N. ;

Nylen, P. .

ACTA MATERIALIA, 2015, 94 :1-14

[23] The influence of bond coat surface roughness and structure on the oxidation of a thermal barrier coating system [J].

Taylor, MP ;

Evans, HE .

HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 5, PTS 1 AND 2, 2001, 369-3 :711-717

[24] Glass-ceramics as oxidation resistant bond coat in thermal barrier coating system [J].

Das, S. ;

Datta, S. ;

Basu, D. ;

Das, G. C. .

CERAMICS INTERNATIONAL, 2009, 35 (04) :1403-1406

[25] Bond coat oxidation and its significance for life expectancy of thermal barrier coating systems [J].

Echsler, H ;

Renusch, D ;

Schütze, M .

MATERIALS SCIENCE AND TECHNOLOGY, 2004, 20 (03) :307-318

[26] On the interfacial degradation mechanisms of thermal barrier coating systems: Effects of bond coat composition [J].

Wu, R. T. ;

Wang, X. ;

Atkinson, A. .

ACTA MATERIALIA, 2010, 58 (17) :5578-5585

[27] Effect of HVOF-sprayed bond coat on the oxidation resistance of thermal barrier coating [J].

Dong Y. ;

Ren Z. ;

Lin X. ;

Wang Z. ;

Ding K. .

Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2010, 46 (20) :86-91

[28] An investigation on high entropy alloy for bond coat application in thermal barrier coating system [J].

Jadhav, Mahesh ;

Singh, Sheela ;

Srivastava, Meenu ;

Kumar, G. S. Vinod .

JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 783 :662-673

[29] Spalling failure of a thermal barrier coating associated with aluminum depletion in the bond-coat [J].

Shillington, EAG ;

Clarke, DR .

ACTA MATERIALIA, 1999, 47 (04) :1297-1305

[30] Defining optimal morphology of the bond coat-thermal barrier coating interface of air-plasma sprayed thermal barrier coating systems [J].

Weeks, Matthew D. ;

Subramanian, Ramesh ;

Vaidya, Anirudha ;

Mumm, Daniel R. .

SURFACE & COATINGS TECHNOLOGY, 2015, 273 :50-59

← 1 2 3 4 5 →