Effects of Silicon Content and Intercritical Annealing on Manganese Partitioning in Dual Phase Steels

被引:32
作者
Nouri, A. [1 ]
Saghafian, H. [1 ]
Kheirandish, Sh [1 ]
机构
[1] Iran Univ Sci & Technol, Dept Met & Mat Engn, Tehran 999067, Iran
关键词
partitioning; dual phase steel; intercritical annealing temperature; silicon; manganese; MECHANICAL-PROPERTIES; AUSTENITE FORMATION; MN; TRANSFORMATION; FERRITE; ALLOYS;
D O I
10.1016/S1006-706X(10)60098-2
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Steels of constant manganese and carbon contents with silicon content of 0. 34%-2. 26% were cast. The as-cast steels were then hot rolled at 1 100 degrees C in five passes to reduce the cast ingot thickness from 80 to 4 mm, air cooled to room temperature and cold rolled to 2 mm in thickness. Dual phase microstructures with different volume fraction of martensite were obtained through the intercritical annealing of the steels at different temperatures for 15 min followed by water quenching. In addition to intercritical annealing temperature, silicon content also altered the volume fraction of martensite in dual phase steels. The partitioning of manganese in dual phase silicon steels was investigated using energy-dispersive spectrometer (EDS). The partitioning coefficient, defined as the ratio of the amounts of alloying element in the austenite to that in the adjacent ferrite, for manganese increased with increasing intercritical annealing temperature and silicon content of steels. It was also found that the solubility of manganese in ferrite and austenite decreased with increasing intercritical temperature. The results were discussed by the diffusivity and the. solubility of manganese in ferrite and austenite existed in dual phase silicon steels.
引用
收藏
页码:44 / 50
页数:7
相关论文
共 20 条
[1]  
AARONSON HI, 1966, T METALL SOC AIME, V236, P768
[2]  
ANDREWS KW, 1965, J IRON STEEL I, V203, P721
[3]   RETAINED AUSTENITE IN A BRINE QUENCHED 0.08-PERCENT C - 0.96-PERCENT MN DUAL PHASE STEEL [J].
CHANG, PH .
SCRIPTA METALLURGICA, 1984, 18 (11) :1245-1250
[4]  
CHATURVEDI MC, 1987, MATER SCI ENG, P1
[5]   INFLUENCE OF SILICON AND PHOSPHORUS ON THE MECHANICAL-PROPERTIES OF BOTH FERRITE AND DUAL-PHASE STEELS [J].
DAVIES, RG .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (01) :113-118
[6]   FORMATION OF AUSTENITE IN 1.5 PCT MN STEELS [J].
GARCIA, CI ;
DEARDO, AJ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1981, 12 (03) :521-530
[7]   METALLOGRAPHY AND PARTITIONING OF ALLOYING ELEMENTS IN DUAL-PHASE STEELS [J].
HOEL, RH .
METALLOGRAPHY, 1984, 17 (03) :273-283
[8]  
KHAIRA HK, 1993, MATER SCI ENG, P267
[9]   PRECIPITATION OF CARBIDES IN LOW-CARBON FE-AL-C ALLOYS [J].
LESLIE, WC ;
RAUCH, GC .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1978, 9 (03) :343-349
[10]   The effect of Mn partitioning in Fe-Mn-Si alloy investigated with STEM-EDS techniques [J].
Lis, J ;
Morgiel, J ;
Lis, A .
MATERIALS CHEMISTRY AND PHYSICS, 2003, 81 (2-3) :466-468