The Zn-rich corner of the Zn-Al-Ti system at 723 K

被引:22
作者
Yang, Sui [1 ,2 ]
Su, Xuping [1 ,3 ]
Wang, Jianhua [1 ]
Yin, Fucheng [1 ]
Li, Zhi [1 ]
Tu, Hao [1 ]
Peng, Haoping [1 ]
机构
[1] Xiangtan Univ, Key Lab Mat Design & Preparat Technol Hunan Prov, Xiangtan 411105, Hunan, Peoples R China
[2] Xiangtan Univ, Fac Mat Optoelect & Phys, Xiangtan 411105, Hunan, Peoples R China
[3] Jiangsu Polytech Univ, Sch Mat Sci & Engn, Changzhou 213164, Jiangsu, Peoples R China
关键词
Zn-Al-Ti system; Phase diagram; Zn-rich corner; Galvanizing; 450-DEGREES-C ISOTHERMAL SECTION; PHASE-DIAGRAM; ALUMINUM-TITANIUM; KINETICS; INTERMETALLICS; COATINGS; SILICON; ALLOYS; TIZN16; GROWTH;
D O I
10.1016/j.jallcom.2010.03.148
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The Zn-rich corner of the Zn-Al-Ti ternary system at 723 K was experimentally determined using equilibrated alloys with the aid of diffusion couple approach. The specimens were investigated by means of optical microscopy, scanning electron microscopy, wave dispersive X-ray spectroscope and X-ray powder diffraction. A true ternary phase T was identified and it is in equilibrium with TiAl3, TiAl2, alpha-Al, liq.Zn. TiZn16, TiZn8 and TiZn in the system respectively. The solubility of Ti in liquid zinc is 0.3 at.%. The solubility of Zn in TiAl3 and TiAl2 is 4.4 at.% and 3.2 at.% respectively and that of Al in TiZn16, TiZn8, TiZn3 and TiZn is 0.4 at.%, 0.2 at.%, 1.7 at.% and 2.5 at.% respectively. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码:194 / 199
页数:6
相关论文
共 49 条
[1]  
Anderson EA, 1944, T AM I MIN MET ENG, V156, P278
[2]  
CALVERT L, 1990, COMMUNICATION
[3]   A THERMODYNAMIC ANALYSIS OF THE AL-ZN SYSTEM AND PHASE-DIAGRAM CALCULATION [J].
CHEN, SL ;
CHANG, YA .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 1993, 17 (02) :113-124
[4]   PREPARATION, PROPERTIES, AND CRYSTAL-STRUCTURES OF TI3ZN22 AND TIZN16 [J].
CHEN, XA ;
JEITSCHKO, W ;
DANEBROCK, ME ;
EVERS, CBH ;
WAGNER, K .
JOURNAL OF SOLID STATE CHEMISTRY, 1995, 118 (02) :219-226
[5]   Control of the growth of zinc-iron phases in the hot-dip galvanizing process [J].
Culcasi, JD ;
Seré, PR ;
Elsner, CI ;
Di Sarli, AR .
SURFACE & COATINGS TECHNOLOGY, 1999, 122 (01) :21-23
[6]   A calorimetric study of alloys along the Ti(Zn, Al)3 section [J].
Delsante, S. ;
Ghosh, G. ;
Borzone, G. .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2009, 33 (01) :50-54
[7]   CRYSTAL STRUCTURE OF TIAL [J].
DUWEZ, P ;
TAYLOR, JL .
JOURNAL OF METALS, 1952, 4 (01) :70-71
[8]  
ERKELENZ V, 1923, E METALL ERZ, V20, P206
[9]   INTERPRETATION OF THE ROLE OF SILICON ON THE GALVANIZING REACTION BASED ON KINETICS, MORPHOLOGY AND THERMODYNAMICS [J].
FOCT, J ;
PERROT, P ;
REUMONT, G .
SCRIPTA METALLURGICA ET MATERIALIA, 1993, 28 (10) :1195-1200
[10]   Contemporary use of Ni and Bi in hot-dip galvanizing [J].
Fratesi, R ;
Ruffini, N ;
Malavolta, M ;
Bellezze, T .
SURFACE & COATINGS TECHNOLOGY, 2002, 157 (01) :34-39