Effect of surface treatment on the dispersion of nano zirconia particles in non-aqueous suspensions for stereolithography

被引：149

作者：

Sun, Jinxing ^{[1
,2
,3
]}

Binner, Jon ^{[3
]}

Bai, Jiaming ^{[1
,2
]}

机构：

[1] Shenzhen Key Lab Addit Mfg High Performance Mat, Shenzhen, Peoples R China

[2] Southern Univ Sci & Technol, Dept Mech & Energy Engn, Shenzhen 518055, Peoples R China

[3] Univ Birmingham, Sch Met & Mat, Birmingham B15 2TT, W Midlands, England

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2019年 / 39卷 / 04期

基金：

中国国家自然科学基金;

关键词：

Nanozirconia; Ceramic suspensions; Dispersants; Rheological behaviour; CERAMICS; FABRICATION; SPECIMENS;

D O I：

10.1016/j.jeurceramsoc.2018.10.024

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Stereolithography (SLA) requires the creation of stable and well dispersed ceramic suspensions with high solid loading in order to achieve dense ceramic parts. Five different dispersants used were stearic acid (SA), oleic acid (OA), Disperbyk (BYK), coupling agent KH560 and variquat CC 42 NS (CC). The results indicated that BYK, KH560 and OA are all capable of creating low viscosity, well dispersed suspensions with nanozirconia particles; of these 3 wt% BYK was the best option. 3 wt% BYK treated suspensions displayed shear thinning behaviour and had a viscosity of 1680 mPa s at a shear rate of 18.6 s(-1). A zirconia part was fabricated using the optimized suspension and its production followed the Beer-Lambert law. After sintering, a significant shrinkage was measured (21.9% in X-Y plane and 28.9% in Z directions), the SEM image showed the sintered part offered a high level of densification.