The Melting Behavior and Thermal Stability of Green Poly(L-lactic acid) with N, N, N, N′-Tetra(benzoyl) Ethylene Diamine Tetraacetic Acid Dihydrazide

The thermal properties of green poly(L-lactic acid) (PLLA) with N, N, N, N'-tetra(benzoyl) ethylene diamine tetraacetic acid dihydrazide (NA) at different conditions were investigated. The melting behavior of PLLA/NA sample after isothermal crystallization at 100 degrees C showed that the low-temperature melting peak shifted to high temperature with increasing of crystallization time. However, the high-temperature melting peak did not show any change. Meantime, the melting enthalpy of cold crystallization was higher than that of hot crystallization, and the difference between cold crystallization and hot crystallization increased from 0.31 J/g to 0.89 J/g with increasing of crystallization time. Heating or cooling rate affected the melting behavior of PLLA, the low-temperature and high-temperature melting peak shifted to low temperature with increasing of rate, and the ratio of melting peak area between low-temperature melting peak and high-temperature melting peak decreased. Thermal stability of PLLA/NA indicated that PLLA/NA only exhibited one decomposition stage as decomposition of PLLA.